Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Modulus | 0.500 GPa @Temperature 100 °C |
72.5 ksi @Temperature 212 °F |
X direction, Condition A; ASTM D695 |
Rogers Corporation RT/duroid® 5880 Glass Microfiber Reinforced PTFE High Frequency Laminate RT/duroid® 5870 and 5880 glass microfiber reinforced PTFE composites are designed for exacting stripline and microstrip circuit applications. Glass reinforcing microfibers are randomly oriented to.. |
|||
Compressive Modulus | 0.500 GPa @Temperature 100 °C |
72.5 ksi @Temperature 212 °F |
Y direction, Condition A; ASTM D695 |
Rogers Corporation RT/duroid® 5880 Glass Microfiber Reinforced PTFE High Frequency Laminate RT/duroid® 5870 and 5880 glass microfiber reinforced PTFE composites are designed for exacting stripline and microstrip circuit applications. Glass reinforcing microfibers are randomly oriented to.. |
|||
Compressive Modulus | 0.500 GPa @Temperature 316 °C |
72.5 ksi @Temperature 601 °F |
ASTM D695 Modified |
Saint-Gobain Meldin® 2021 Bearing General Notes on Meldin 2000 Series Bearing Products:For High-Temperature, Close-Tolerance Applications. Able to withstand temperatures of 600°F with excursions to 900°F, the Medlin 2000 Series ca.. |
|||
Compressive Modulus | 0.500 GPa @Temperature 260 °C |
72.5 ksi @Temperature 500 °F |
ASTM D695 Modified |
Saint-Gobain Meldin® 2030 Bearing General Notes on Meldin 2000 Series Bearing Products:For High-Temperature, Close-Tolerance Applications. Able to withstand temperatures of 600°F with excursions to 900°F, the Medlin 2000 Series ca.. |