Saint-Gobain Meldin® 2030 Bearing
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Saint-Gobain Perfomance Plastics |
| Trade Name | Meldin® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Saint-Gobain Meldin® 2030 Bearing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Notes on Meldin 2000 Series Bearing Products:For High-Temperature, Close-Tolerance Applications. Able to withstand temperatures of 600°F with excursions to 900°F, the Medlin 2000 Series can be machined into various confiations, from rod or sheet stock shapes. Black in color. Meldin 2000 Series offers very high compression strength, high creep resistance, and dimensional stability.Specific Notes on Meldin 2030 BearingMeldin 2030 bearing compound operates with extremely low friction in both dynamic and static applications, and provides thermal and electrical insulation.Applications include: Appliances, Automotive, Industrial, Semiconductor, Transportation.Specification Notes: Bushing MaterialInformation provided by Saint Gobain Performance Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Water Absorption | 0.62 % | 0.62 % | ASTM D570 |
| Deformation | 0.35 % @Pressure 13.8 MPa |
0.35 % @Pressure 2000 psi |
24 hrs. Mold Direction; ASTM D621 |
| Outgassing - Total Mass Loss | 0.00 % | 0.00 % | % CVCM; ASTM E55955 |
| 1.15 % | 1.15 % | % WVR; ASTM E595 | |
| 1.25 % | 1.25 % | % TML; ASTM E5955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | ASTM D2240 |
| Tensile Strength, Ultimate | 3.40 MPa @Temperature 316 °C |
493 psi @Temperature 601 °F |
ASTM D 638 |
| 13.7 MPa @Temperature 260 °C |
1990 psi @Temperature 500 °F |
ASTM D 638 | |
| 27.5 MPa @Temperature 23.0 °C |
3990 psi @Temperature 73.4 °F |
ASTM D 638 | |
| Elongation at Break | 2.8 % @Temperature 260 °C |
2.8 % @Temperature 500 °F |
ASTM D 638 |
| 4.0 % @Temperature 316 °C |
4.0 % @Temperature 601 °F |
ASTM D 638 | |
| 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
ASTM D 638 | |
| Tensile Modulus | 0.0600 GPa @Temperature 316 °C |
8.70 ksi @Temperature 601 °F |
ASTM D 638 |
| 0.600 GPa @Temperature 23.0 °C |
87.0 ksi @Temperature 73.4 °F |
ASTM D 638 | |
| 0.600 GPa @Temperature 260 °C |
87.0 ksi @Temperature 500 °F |
ASTM D 638 | |
| Flexural Strength | 48.2 MPa | 6990 psi | ASTM D 790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D 790 |
| Compressive Yield Strength | 22.0 MPa @Strain 6.00 %, Temperature 316 °C |
3190 psi @Strain 6.00 %, Temperature 601 °F |
ASTM D695 Modified |
| 38.0 MPa @Strain 7.00 %, Temperature 260 °C |
5510 psi @Strain 7.00 %, Temperature 500 °F |
ASTM D695 Modified | |
| 117 MPa @Strain 10.0 %, Temperature 23.0 °C |
17000 psi @Strain 10.0 %, Temperature 73.4 °F |
ASTM D695 Modified | |
| Ultimate Compressive Strength | 34.4 MPa @Temperature 316 °C |
4990 psi @Temperature 601 °F |
ASTM D695 Modified |
| 55.1 MPa @Temperature 260 °C |
7990 psi @Temperature 500 °F |
ASTM D695 Modified | |
| 137.8 MPa @Temperature 23.0 °C |
19990 psi @Temperature 73.4 °F |
ASTM D695 Modified | |
| Compressive Modulus | 0.300 GPa @Temperature 316 °C |
43.5 ksi @Temperature 601 °F |
ASTM D695 Modified |
| 0.500 GPa @Temperature 260 °C |
72.5 ksi @Temperature 500 °F |
ASTM D695 Modified | |
| 1.30 GPa @Temperature 23.0 °C |
189 ksi @Temperature 73.4 °F |
ASTM D695 Modified | |
| Izod Impact, Notched | 0.182 J/cm | 0.341 ft-lb/in | ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 59.0 µm/m-°C | 32.8 µin/in-°F | ASTM E831-93 |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | C518/C177 |
| Maximum Service Temperature, Air | >= 316 °C | >= 600 °F | UL-746 B |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 2.98 @Frequency 1.00e+6 Hz |
2.98 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.02 @Frequency 10000 Hz |
3.02 @Frequency 10000 Hz |
ASTM D150 | |
| 3.03 @Frequency 100 Hz |
3.03 @Frequency 100 Hz |
ASTM D150 | |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Dissipation Factor | 0.0012 @Frequency 100 Hz |
0.0012 @Frequency 100 Hz |
ASTM D150 |
| 0.0031 @Frequency 10000 Hz |
0.0031 @Frequency 10000 Hz |
ASTM D150 | |
| 0.0049 @Frequency 1.00e+6 Hz |
0.0049 @Frequency 1.00e+6 Hz |
ASTM D150 |