Polymer Property : Tensile Strength, Ultimate = 113000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	779 MPa @Thickness 12.7 mm, Temperature 538 Â°C	113000 psi @Thickness 0.500 in, Temperature 1000 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	779 MPa @Thickness 19.0 mm, Temperature 538 Â°C	113000 psi @Thickness 0.750 in, Temperature 1000 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	776 MPa @Temperature 425 Â°C	113000 psi @Temperature 797 Â°F	AMS 5879
Haynes 625SQÂ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200Â°F (649Â..
Tensile Strength, Ultimate	776 MPa @Temperature 540 Â°C	113000 psi @Temperature 1000 Â°F	AMS 5879
Haynes 625SQÂ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200Â°F (649Â..
Tensile Strength, Ultimate	779 MPa @Thickness 6.35 mm	113000 psi @Thickness 0.250 in
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	778 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	113000 psi @Thickness 0.500 in, Temperature 77.0 Â°F
Haynes HastelloyÂ® C-2000Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	778 MPa @Thickness 3.20 mm, Temperature 427 Â°C	113000 psi @Thickness 0.126 in, Temperature 801 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	779 MPa @Temperature 538 °C	113000 psi @Temperature 1000 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate	779 MPa @Temperature 538 °C	113000 psi @Temperature 1000 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate	780 MPa @Thickness 25.4 mm, Temperature 25.0 °C	113000 psi @Thickness 1.00 in, Temperature 77.0 °F	as welded
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..
Tensile Strength, Ultimate	778 MPa @Thickness 19.1 mm, Temperature 93.0 °C	113000 psi @Thickness 0.752 in, Temperature 199 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate	779 MPa @Temperature 25.0 °C	113000 psi @Temperature 77.0 °F
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed..