Polymer Property : Flexural Yield Strength = 7830 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	54.0 MPa	7830 psi	ASTM D790
North Wood Plastics Polypropylene with 40% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc.
Flexural Yield Strength	54.0 - 54.0 MPa @Temperature 250 - 250 °C	7830 - 7830 psi @Temperature 482 - 482 °F	Average value: 54.0 MPa Grade Count:1
Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and m..
Flexural Yield Strength	54.0 - 167 MPa	7830 - 24200 psi	Average value: 111 MPa Grade Count:43
Overview of materials for Polystyrene + Polyphenylene Ether, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Unreinforced". Each property range of values reported is minimum and ..
Flexural Yield Strength	54.0 MPa	7830 psi	15 mm/min; ASTM D790
LG Chemical SG-950 Alphalac Polystyrene High strength, High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include housing of electr..
Flexural Yield Strength	54.0 MPa	7830 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP HAL23 PA11 (Europe-Africa-Middle East) LNP* LUBRICOMP* HAL23 is a compound based on PA 11 resin containing Aramid Fiber, PTFE. Added features include: Internally Lubricated.
Flexural Yield Strength	54.0 MPa	7830 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP MG004 PP (Europe-Africa-Middle East) LNP* Lubricomp* MG004 is a compound based on Polypropylene resin containing Graphite Powder.
Flexural Yield Strength	54.0 MPa	7830 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A3000TXB ABS LNP* STAT-LOY* A3000TXB is a compound based on ABS resin. Added features of this material include: Antistatic, Transparent, Formulated with FDA Food Contact Additives and Bioassessed to ISO 10993...
Flexural Yield Strength	54.0 MPa	7830 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp FF004 PE LNP THERMOCOMP* FF004 is a compound based on Polyethylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	54.0 MPa	7830 psi	ASTM D790
E-Polymers Tekaloy® T80FR , Flame Retardant Un-Reinforced PBT/ABS Alloy Flame RetardantInformation provided by E-Polymers Co. Ltd.