SABIC Innovative Plastics LNP Thermocomp FF004 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp FF004 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* FF004 is a compound based on Polyethylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D 792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D 638 | |
| 40.0 MPa | 5800 psi | ASTM D 638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
| 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 4.2 % | 4.2 % | 5 mm/min; ISO 527 |
| 4.3 % | 4.3 % | ASTM D 638 | |
| 4.6 % | 4.6 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.42 GPa | 496 ksi | 1 mm/min; ISO 527 |
| 4.21 GPa | 611 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D 790 |
| 51.0 MPa | 7400 psi | ISO 178 | |
| Flexural Yield Strength | 54.0 MPa | 7830 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D 790 |
| 2.84 GPa | 412 ksi | 2 mm/min; ISO 178 | |
| 2.98 GPa | 432 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.650 J/cm @Temperature 23.0 °C |
1.22 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.37 J/cm @Temperature 23.0 °C |
6.31 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 56.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
31.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 123 µm/m-°C @Temperature -30.0 - 30.0 °C |
68.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |