- Polymer Property : Fracture Toughness = 3.64 ksi-in½
Polymer Property : Fracture Toughness = 3.64 ksi-in½ Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | |
| ICE Hot Pressed SiC Data provided by the manufacturer, International Ceramic Engineering. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | ASTM C1421 |
| M Cubed Technologies SSC-702 Reaction-Bonded Silicon Carbide Medium-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | ASTM C1421 |
| M Cubed Technologies SSC-802 Reaction-Bonded Silicon Carbide Medium-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | ASTM C1421 |
| M Cubed Technologies SSC-FG Reaction-Bonded Silicon Carbide, Fine-Grained Fine-grained reaction-bonded SiC. Used for mechanical seals and other SiC applications that require a high surface finish/tight tolerances. Si content can be tailored for the application.Informati.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | K<sub>IC</sub> (SEVNB); DIN CEN/TS 14425-1 |
| CeramTec Rocar® SiG Silicon Carbide, SiSiC Rocar® is an extremely lightweight silicon carbide ceramic. It permits a reduction in mass forces at high speeds, and is considered for its hardness, excellent resistance to corrosion and sudden ch.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | K<sub>IC</sub>; DIN 51109 |
| CeramTec Rubalit® IS 95 Alumina Rubalit® IS 95 is a high-performance alumina ceramic. Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at eleva.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | K<sub>IC</sub> (SEVNB); DIN CEN/TS 14425-1 |
| CeramTec V 38 Alumina, 96.0% Al2O3-SiO2 Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | ASTM C1421 |
| M Cubed Technologies SSC-903 Reaction-Bonded Silicon Carbide Coards-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | |
| CoorsTek AD-94 Alumina (nom. 94% Al2O3) Thermal Shock Delta Tc = 250°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | |
| CoorsTek AD-995 Alumina (nom. 99.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Klc; Notched Beam |
| CoorsTek AD-996 99.6% Alumina |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | |
| CoorsTek AD-998 Alumina(nom. 99.8% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Klc; Notched Beam |
| CoorsTek CAP 3 99.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Klc; Notched Beam |
| CoorsTek CAP 4 98.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | |
| CoorsTek Direct Sintered Silicon Carbide, SC DS (SC-30, UltraSiC™) Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Klc; Notched Beam |
| CoorsTek FG-98 98% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | |
| CoorsTek FG-995 Alumina (nom. 98.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Notched Beam |
| CoorsTek PlasmaPure™ Alumina (nom. 99.8% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Klc; Notched Beam |
| CoorsTek PlasmaPure-UC™ 99.9% Alumina |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | |
| CoorsTek Reaction Bonded Silicon Carbide, SCRB (SC-2) Thermal Shock Delta Tc = 400°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Klc; Notched Beam |
| CoorsTek Z-PLUS™ 94 Zirconia-Impr. Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | DIN 51109 |
| CeramTec 975 Alumina, 99.5% 975 (99.5%) offers unique technology by virtue of its optimal dispersion of the MgO phase with the alumina grains. With virtually no transgranular porosity in its microstructure, 975 exhibits high d.. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | K<sub>IC</sub> (SEVNB); DIN CEN/TS 14425-1 |
| CeramTec AT 79 Alumina, 99.6% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | K<sub>IC</sub>; DIN 51109 |
| CeramTec Rubalit® IS 95 Brown Alumina Rubalit® IS 95 brown is a high-performance alumina ceramic. Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at.. |
|||