CoorsTek PlasmaPure™ Alumina (nom. 99.8% Al2O3)
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CoorsTek |
| Trade Name | PlasmaPure™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CoorsTek PlasmaPure™ Alumina (nom. 99.8% Al2O3).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a sharp decrease in the flexural strength of the sample.Data Provided by the manufacturer, CoorsTek, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.93 g/cc | 0.142 lb/in³ | ASTM C20 |
| Water Absorption | 0.00 % | 0.00 % | ASTM 373 |
| Particle Size | 6.0 µm | 6.0 µm | Thin Section Crystal Size |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Knoop Microhardness | 14.1 | 14.1 | 1000 g |
| Hardness, Rockwell 45 N | 83 | 83 | |
| Tensile Strength, Ultimate | 275 MPa | 39900 psi | ACMA Test #4 |
| Modulus of Elasticity | 370 GPa | 53700 ksi | ASTM C848 |
| Flexural Strength | 400 MPa | 58000 psi | ASTM F417 |
| Compressive Strength | 2680 MPa | 389000 psi | ASTM C773 |
| Poissons Ratio | 0.22 | 0.22 | ASTM C848 |
| Fracture Toughness | 4.00 - 5.00 MPa-m½ | 3.64 - 4.55 ksi-in½ | Notched Beam |
| Shear Modulus | 152 GPa | 22000 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
| Specific Heat Capacity | 0.880 J/g-°C | 0.210 BTU/lb-°F | ASTM E1269 |
| Thermal Conductivity | 30.0 W/m-K | 208 BTU-in/hr-ft²-°F | ASTM C408 |
| Maximum Service Temperature, Air | 1750 °C | 3180 °F | No Load |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D1829 |
| 3.00e+6 ohm-cm @Temperature 1000 °C |
3.00e+6 ohm-cm @Temperature 1830 °F |
ASTM D1829 | |
| 1.00e+11 ohm-cm @Temperature 500 °C |
1.00e+11 ohm-cm @Temperature 932 °F |
ASTM D1829 | |
| Dielectric Constant | 9.8 @Frequency 1e+6 Hz |
9.8 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 8.70 kV/mm | 221 kV/in | AC; ASTM D116 |
| Dissipation Factor | <= 0.00010 @Frequency 1e+6 Hz |
<= 0.00010 @Frequency 1e+6 Hz |
ASTM D2520 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Ivory |
Users viewing this material also viewed the following:
- PolyOne Bergadur™ PB40 G15 UF UV Polybutylene Terephthalate (PBT)
- Kennametal Stellite Stellite® 6K 1.6 mm thick sheet
- SK Chemicals SKYTHANE® US518 Adhesive (Dry Lamination)
- Styron CALIBREâ„¢ MEGARAD 2080 10 Polycarbonate, Gamma Radiation Resistant
- Engineered Syntactic Systems MZ-24 Deep Water Syntactic Foam
- Fainplast Compounds CL 68 Flexible PVC, Sheathing
- California Fine Wire Nickel Alloy 99
- Ashley Polymers Ashlene® D925 Nylon 12
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Zinc Stearate
Copyright © lookpolymers.com All Rights Reserved