Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Fracture Toughness | 13.0 MPa-m½ | 11.8 ksi-in½ | |
ICE ZrO Data provided by the manufacturer, International Ceramic Engineering. |
|||
Fracture Toughness | 13.0 MPa-m½ | 11.8 ksi-in½ | ASTM C1421 |
M Cubed Technologies MMC-S55 Aluminum alloy-55% SiC Metal Matrix Composite High stiffness, low density composite. Parts are cast using several standard foundry techniques Size range varies from small components (1lb or smaller) to parts greater than 10 ft. square with co.. |
|||
Fracture Toughness | 13.0 MPa-m½ | 11.8 ksi-in½ | Notched Beam |
CoorsTek Yttria Partially Stabilized Zirconia, YZTP, Sintered Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Fracture Toughness | 13.0 MPa-m½ | 11.8 ksi-in½ | Notched Beam |
CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |