Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 5.96 GPa @Temperature 23.0 °C |
864 ksi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Crastin® CE15315 NC010 PBT
(Unverified Data**) Crastin® CE15315 NC010 is a 15% glass reinforced flame retardant polybutylene terephthalate molding resin. It is recognized as UL94 V-0 at 0.71mm(0.028in).Information provided by DuPont Performance.. |
|||
Tensile Modulus | 5.96 GPa | 864 ksi | same value from ASTM and ISO test. |
BASF Capron® 8231G 14% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8231G is a 14% glass fiber reinforced polyamide 6 molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics. It is also av.. |
|||
Tensile Modulus | 5.96 GPa | 864 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66 LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
Tensile Modulus | 5.96 GPa | 864 ksi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® CE15315 NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)&l 15% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin CE15315 NC010 is a 15% glass reinforced flame retardant polybutylene terephthalate molding resin. It is recognized as UL94 V-0.. |
|||
Tensile Modulus | 5.96 GPa | 864 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry) Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The gla.. |