DuPont Performance Polymers Crastin® CE15315 NC010 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® CE15315 NC010 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® CE15315 NC010 is a 15% glass reinforced flame retardant polybutylene terephthalate molding resin. It is recognized as UL94 V-0 at 0.71mm(0.028in).Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.499 g/cc
0.05415 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 2.00 mm
0.0030 - 0.0050 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 - 0.0090 cm/cm

@Thickness 2.00 mm
0.0050 - 0.0090 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 101 MPa

@Temperature 23.0 °C
14600 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 3.1 %

@Temperature 23.0 °C
3.1 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 5.96 GPa

@Temperature 23.0 °C
864 ksi

@Temperature 73.4 °F
ISO 527
Charpy Impact Unnotched 3.01 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
3.18 J/cm²

@Temperature 23.0 °C
15.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.620 J/cm²

@Temperature -30.0 °C
2.95 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.620 J/cm²

@Temperature 23.0 °C
2.95 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 223 °C
433 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
UL RTI, Electrical 130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
UL 746B
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746B
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical with Impact 110 °C

@Thickness 0.710 mm
230 °F

@Thickness 0.0280 in
UL 746B
110 °C

@Thickness 1.50 mm
230 °F

@Thickness 0.0591 in
UL 746B
120 °C

@Thickness 3.00 mm
248 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact 130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746B
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746B
130 °C

@Thickness 0.710 mm
266 °F

@Thickness 0.0280 in
UL 746B
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL94
V-0

@Thickness 0.710 mm
V-0

@Thickness 0.0280 in
UL94
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Optimum; Injection Molding
240 - 260 °C
464 - 500 °F
Injection Molding
Mold Temperature 60.0 °C
140 °F
optimum; Injection Molding
10.0 - 110 °C
50.0 - 230 °F
Injection Molding
Drying Temperature 100 - 140 °C
212 - 284 °F
Injection Molding
Dry Time 2.00 - 6.00 hour
2.00 - 6.00 hour
Injection Molding
Moisture Content <= 0.040 %
<= 0.040 %
Injection Molding
Descriptive Properties Value Comments
Forms Pellets
Generic PBT
Material Status Current
Part Marking Code >PBT-GF15FR(17)<
ISO 11469
Processing Method Injection Molding
Product Category Extrusion Resins
Glass Reinforced Resins
Resin Identification PBT-GF15FR(17)
ISO 1043
RoHS Compliance Contact Manufacturer