Polymer Property : Tensile Strength, Yield = 189000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 1300 MPa	>= 189000 psi	After bake hardening
SSAB Tunnplat DocolÂ® 1400 DP High-strength Steel The steels are annealed at temperatures between 750Â°C and 850Â°C, depending on the grade of steel, and then are hardened by quenching in water. Tempering is the next stage, in which the steel ..
Tensile Strength, Yield	1300 MPa	189000 psi
ThyssenKrupp XAR® 500 Structural Steel This Material Specification applies to 3 to 100 mm thick plates of the wear-resistant special structural steel XAR® 500.Application: The steel may be used for wear exposed structures, e.g. excavati..
Tensile Strength, Yield	1300 MPa	189000 psi
ThyssenKrupp SECURE 500 Structural Steel This Material Specification applies to the alloyed, liquid-quenched and tempered high-strength special steel SECURE 500 for civil use, that is usually produced in thickness from 3 mm up to 90 mm.App..
Tensile Strength, Yield	1300 MPa	189000 psi
Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High ..
Tensile Strength, Yield	1303 MPa @Strain 0.200 %, Temperature -40.0 °C	189000 psi @Strain 0.200 %, Temperature -40.0 °F
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1100 (Heated 593°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio..
Tensile Strength, Yield	1303 MPa @Strain 0.200 %	189000 psi @Strain 0.200 %
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good ..
Tensile Strength, Yield	1303 MPa @Strain 0.200 %	189000 psi @Strain 0.200 %
ATI Allvac® VascoJet® 1000 Specialty Steel, Heat Treatment: 1010°C (1850°F) Q+T Data provided by Allvac.Applications: Landing gear components, springs, fasteners. Gears and shafts for helicopter applications.