Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 1300 MPa | >= 189000 psi | After bake hardening |
SSAB Tunnplat Docol® 1400 DP High-strength Steel The steels are annealed at temperatures between 750°C and 850°C, depending on the grade of steel, and then are hardened by quenching in water. Tempering is the next stage, in which the steel .. |
|||
Tensile Strength, Yield | 1300 MPa | 189000 psi | |
ThyssenKrupp XAR® 500 Structural Steel This Material Specification applies to 3 to 100 mm thick plates of the wear-resistant special structural steel XAR® 500.Application: The steel may be used for wear exposed structures, e.g. excavati.. |
|||
Tensile Strength, Yield | 1300 MPa | 189000 psi | |
ThyssenKrupp SECURE 500 Structural Steel This Material Specification applies to the alloyed, liquid-quenched and tempered high-strength special steel SECURE 500 for civil use, that is usually produced in thickness from 3 mm up to 90 mm.App.. |
|||
Tensile Strength, Yield | 1300 MPa | 189000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |