SABIC Innovative Plastics LNP LUBRICOMP EFL24P PEI

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP EFL24P PEI.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* EFL24P is a compound based on Polyetherimide resin containing 20% Glass Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Exceptional Processing.

Physical Properties	Metric	English	Comments
Specific Gravity	1.48 g/cc	1.48 g/cc	ASTM D792
Moisture Absorption	0.180 %	0.180 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm @Thickness 3.20 mm	0.0020 - 0.0030 in/in @Thickness 0.126 in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	146 MPa	21200 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	2.3 %	2.3 %	5 mm/min; ISO 527
Flexural Strength	190 MPa	27600 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	6.47 GPa	938 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched (ISO)	78.0 kJ/mÂ²	37.1 ft-lb/inÂ²	80104; ISO 180/1A
Coefficient of Friction, Dynamic	0.43	0.43	ASTM D3702 Modified
Coefficient of Friction, Static	0.41	0.41	ASTM D3702 Modified
K (wear) Factor	310 x 10^-8 mmÂ³/N-M	154 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	213 Â°C @Thickness 3.20 mm	415 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257