Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527, ASTM D638 |
Nilit Nilamid A G5 FR PH2 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous) Description: Nilamid A G5 FR PH2 combines flame retardancy with outstanding mechanical performance. This product has a complete yellow card, with RTI and CTI listings. The formulation has been optim.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527, ASTM D638 |
Nilit Nilitop BT G6 FR C3 is a 30% Glass Fiber Reinforced, Flame Retardant PBT Description: Nilitop BT G6 FR C3 is a 30% glass fiber reinforced, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive. It.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527-1/2 |
Radici Radilon® SERV3808 K (dry) Nylon 6 Heat stabilized glass-fiber reinforced with high impact strengthInformation provided by Radici group. |
|||
Tensile Strength, Yield | 130 - 150 MPa | 18900 - 21800 psi | Average value: 141 MPa Grade Count:4 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527, ASTM D638 |
Nilit Nilamid B G6 FR C4 30% Glass Fiber Reinforced, Flame Retardant PA6 Description: Nilamid B G6 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
Tensile Strength, Yield | 130 - 265 MPa | 18900 - 38400 psi | Average value: 212 MPa Grade Count:54 |
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Tensile Strength, Yield | 130 - 210 MPa | 18900 - 30500 psi | |
Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; A (TB00) Temper; All Thicknesses (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Yield | 130 - 250 MPa | 18900 - 36300 psi | |
Materion Beryllium Copper Alloy 25 Tube; A (TB00) Temper; All Sizes (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Yield | 130 - 210 MPa | 18900 - 30500 psi | |
Materion Beryllium Copper Alloy 25 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Yield | 130 - 280 MPa | 18900 - 40600 psi | |
Materion Beryllium Copper Alloy 3 Forgings & Extrusions; A (TB00) Temper (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Yield | 130 MPa @Strain 0.200 %, Temperature 980 °C |
18900 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Yield | 130 MPa @Strain 0.200 %, Temperature 980 °C |
18900 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2200N PEI 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2200N PEI (Europe-Africa-Middle East) 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX04489C PC LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Con.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East) VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and light.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
Polyram PlusTek PA301G3 Nylon 6.6, Heat Stabilized, 15% Glass Fiber Heat stabilized, 15% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | >= 130 MPa | >= 18900 psi | ASTM-D638 |
Polyram PlusTek RB300G6 Nylon 6, 30% Glass Fiber 30% glass-fiber reinforced polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | >= 130 MPa | >= 18900 psi | ISO 527 |
Polyram PlusTek RB301G6 Nylon 6 for Injection Molding, 30% Glass-fiber Reinforced, Industrial Grade Industrial grade, 30% glass-fiber reinforced Nylon 6 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
Polyram PlusTek RD302G6 Nylon 12, 30% Glass Fiber 30% glass-fiber reinforced polyamide 12 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
Polyram PlusTek RA307G4 Nylon 6.6, 20% Glass Fiber 20% glass fiber reinforced heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
Polyram RamTough PZ300G8 Polycarbonate, 40% Glass Fiber 40% Glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527 |
Chevron Phillips Xtel® XE4050BL Polyphenylene Sulfide Alloy Xtel® XE4050BL is a glass fiber and mineral filled PPS based alloy developed to provide high ductility and impact strength along with good thermal stability.Information provided by Chevron Phillips.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | D638 |
Ensinger Tecapeek® ST PolyEtherKetoneEtherKetoneKetone, Unreinforced TECAPEEK® ST is a multipurpose semi-crystaline material from the polyaryletherketone family based on PEKEKK that features improved mechanical properties at higher temperatures. The benefits of TECA.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | 50 mm/min; ISO 527-2 |
BASF Ultradur® B 4300 G6 HR 30% Glass Filled PBT Description: Is a PBT, injection-molding grade with 30% glass fibers; for rigid and dimensionally stable technical parts with increased requirements on hydrolysis resistance, e.g. automotive connect.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | 50mm/min; ISO 527 |
BASF Ultramid® A3EG6 30% Glass Filled PA66 (Conditioned) Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® A3WG6 BK 00564 30% Glass Filled PA66 (Conditioned) Description: 30% glass-fiber reinforced and heat aging resistant injection-molding grade for machine elements and housings of high stiffness and dimensional stability such as lamp socket housings, f.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® A3X4G7 35% Glass Filled PA66 FR (Dry) Description: 35% glass-fiber reinforced injection-molding grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stiffness and stre.. |
|||
Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
Polyram RamSter PF392G6 PBT, 30% Glass Fiber 30% glass-fiber reinforced, surface modified PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |