Polymer Property : Tensile Strength, Yield = 1010 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	1010 MPa @Strain 0.200 %	146500 psi @Strain 0.200 %
International Mold Steel NAK55 Precipitation Hardened Mold Steel Description: NAK55 is a precipitation, or age-hardened mold steel with a through hardness of approximately 40 HRc. NAK55 is ideal for use in plastic and rubber molds and other applications where imp..
Tensile Strength, Yield	1010 MPa @Strain 0.200 %	146000 psi @Strain 0.200 %
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete..
Tensile Strength, Yield	1010 MPa @Strain 0.200 %, Temperature 20.0 °C	146000 psi @Strain 0.200 %, Temperature 68.0 °F	Longitudinal Tests from 6.3" rolled plate at 375 HB
EDRO EDRO400™ #40 Prehardened Insert Quality Martensitic Stainless Steel EDRO400™ is a remelted 400 series martensitic stainless steel supplied prehardened to 40 HRC (375 HB).EDRO400™ is characterized by excellent polishability, superior corrosion resistance, high leve..
Tensile Strength, Yield	1010 MPa	146000 psi	40% Cold Worked
ATI Allegheny Ludlum Allcorr® Nickel-Based, Corrosion Resistant Alloy Characteristics: non-age hardenable; outstanding resistance to general corrosion, pitting corrosion, crevice corrosion, intergranular corrosion, and stress corrosion cracking; high strength; high du..
Tensile Strength, Yield	1010 MPa @Strain 0.200 %	146000 psi @Strain 0.200 %
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 30% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co..