Polymer Property : Film Tensile Strength at Break, MD = 56.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	ASTM D882
Westlake Mxsten CV CV77515-F Plastomer (discontinued **) Mxsten CV plastomer CV77515-X is a polyethylene plastomer designed for blown film extrusion that contains medium slip and no antiblock additives. Films produced with this resin exhibit a very low s..
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	ISO 1184
SIDPEC EGYPTENEÂ® HD 5301 FB HDPE Film Applications:Strong thin filmCarrier bagGrocery sacksFilm properties were measured on 15 micron film extruded at a blow up ratio of 5:1, 8D neck height.Information provided by Interchim s.r.l., offi..
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	ASTM-D882
Westlake Mxsten CV77515 Polyethylene Plastomer Mxsten CV Plastomer CV77515 resin is a polyethylene plastomer designed for blown film extrusion and food packaging that contains 1,000 ppm slip and no antiblock additives. Films produced with this r..
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	ASTM D882
Eastman Eastar A150 Copolyester, Film Eastar A150 Copolyester is a poly(1,4-cyclohexylene-dimethylene terephthalate/isophthalate). It is produced by reacting terephthalic acid and isophthalic acid with the glycol 1,4-cyclohexanedimethan..
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	Calculated from mfr's report of 165 N/cm per ASTM D828 and the typical thickness
DuPont™ Nomex® E56 Paper, 12 mil Nominal Thickness Nomex® Type E56 is designed for cost critical uses which require lesser amounts of mechanical and electrical strength than other Nomex® grades. It is thermally similar to Nomex® Type 410 but as..
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	ASTM D882
NOVA Chemicals Sclair® 11C1 Octene LLDPE Film Resin (discontinued **) Low gel, Good processability, Excellent mechanical propertiesApplications: Shrink filmAdditives: Process stabilizerFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but ..
Film Tensile Strength at Break, MD	56.0 MPa	8120 psi	ISO 527-3
Borealis Borstar® FB4370 Medium Density Polyethylene Borstar® FB4370 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Applications: Borstar® FB4370 has been developed especially for ap..