Polymer Property : Film Tensile Strength at Break, MD = 2180 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	15.0 - 31.0 MPa	2180 - 4500 psi	Average value: 24.0 MPa Grade Count:12
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade". Each property range of values reported..
Film Tensile Strength at Break, MD	15.0 - 40.0 MPa	2180 - 5800 psi	Average value: 27.1 MPa Grade Count:145
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Film Grade". Each property range of values reported is minimum a..
Film Tensile Strength at Break, MD	15.0 MPa	2180 psi	ISO 527
Inno-Comp INNOPOLÂ® CS 5-8250 W 50% Chalk-Filled High Density Polyethylene INNOPOLÂ® CS 5-8250 W is a 50% chalk-filled compound based on high density polyethylene.INNOPOLÂ® CS 5-8250 W is developed for packaging film production.All information provided by INNO-COMP.
Film Tensile Strength at Break, MD	15.0 - 193 MPa	2180 - 28000 psi	Average value: 121 MPa Grade Count:382
Overview of materials for Polypropylene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Film Grade". Each property range of values reported is minimum and maximum values of appr..