Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 |
ExxonMobil LD 146.NH Cast Film Resin
(discontinued **) LD 146.NH is a homopolymer film resin offering good clarity, toughness, and stiffness. It is used in food packaging and laminating film.Information provided by ExxonMobil Chemical |
|||
Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 |
ExxonMobil LD 146.NH Packaging Film Resin
(discontinued **) LD 146.NH is a homopolymer film resin offering good clarity, toughness, and stiffness. It is used in food packaging and laminating film.Information provided by ExxonMobil Chemical |
|||
Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | Cast; ASTM D822 |
LyondellBasell Petrothene® NA373244 Low Density Polyethylene, Cast/Blown Film Grade ApplicationsPetrothene NA373 is a series of homopolymer resins selected by customers for use in household film and other applications that require high clarity and good impact strength combined with.. |
|||
Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | Cast; ASTM D822 |
LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade ApplicationsPetrothene NA373 is a series of homopolymer resins selected by customers for use in household film and other applications that require high clarity and good impact strength combined with.. |
|||
Film Tensile Strength at Yield, MD | 9.38 - 11.0 MPa | 1360 - 1600 psi | Average value: 10.3 MPa Grade Count:3 |
Overview of materials for Low Density Polyethylene (LDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Blow Molding Grade". Each property range of values reported is minimum .. |
|||
Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 |
ExxonMobil LL 1001x59 Blown Film Resin
(discontinued **) LL1001 are butene LLDPE blown film resins having good drawdown, tensile and toughness properties.Information provided by ExxonMobil Chemical |