ExxonMobil LL 1001x59 Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 1001x59 Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LL1001 are butene LLDPE blown film resins having good drawdown, tensile and toughness properties.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil Method
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.38 MPa
1360 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 9.51 MPa
1380 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 580 %
580 %
ASTM D882
Film Elongation at Break, TD 850 %
850 %
ASTM D882
Puncture Energy 3.13 J
2.31 ft-lb
ExxonMobil
Elmendorf Tear Strength, MD 3.15 g/micron
80.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 15.7 g/micron
400 g/mil
ASTM D1922
Dart Drop 4.09 g/micron
104 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 53.1 MPa
7700 psi
ASTM D882
Film Tensile Strength at Break, TD 35.3 MPa
5120 psi
ASTM D882
1% Secant Modulus, MD 193 MPa
28000 psi
ASTM D882
1% Secant Modulus, TD 223 MPa
32300 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 121 °C
249 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 15.3 %
15.3 %
ASTM D1003
Gloss 45 %
45 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer