Polymer Property : Film Tensile Strength at Yield, MD = 2900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	20.0 MPa	2900 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PS 1324 PRE-ELEC PS 1324 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ..
Film Tensile Strength at Yield, MD	20.0 - 30.0 MPa	2900 - 4350 psi	Average value: 26.0 MPa Grade Count:6
Overview of materials for Styrene-Butadiene Copolymer, SBC This property data is a summary of similar materials in the MatWeb database for the category "Styrene-Butadiene Copolymer, SBC". Each property range of values reported is minimum and maximum values ..
Film Tensile Strength at Yield, MD	20.0 MPa	2900 psi	ISO 527-3
EMS-Grivory Grivory® CA 6 E PA* Product description: Grilon CA 6 E is a non-extracted copolyamide with a low melting point. Grilon CA 6 E characterizes itself through the following properties Very high flexibility and toughnessVer..
Film Tensile Strength at Yield, MD	20.0 - 37.0 MPa	2900 - 5370 psi	Average value: 28.0 MPa Grade Count:10
Overview of materials for Polypropylene, Sheet/Thermoforming Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum..
Film Tensile Strength at Yield, MD	20.0 MPa	2900 psi	ASTM D882
Braskem HF 0144 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras..
Film Tensile Strength at Yield, MD	20.0 MPa	2900 psi	2 in per min; ASTM D882
Chevron Phillips K-Resin® DK13 Styrene-Butadiene Copolymer, Film Grade (discontinued **) Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: DK13 is an SBC designed for the film market and has i..