Polymer Property : Tensile Strength, Yield = 455 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	455 MPa @Temperature 21.1 °C	66000 psi @Temperature 70.0 °F	0° Direction, Dry; ASTM D638
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Tensile Strength, Yield	455 MPa @Diameter 12.7 mm	66000 psi @Diameter 0.500 in	As welded; 0.2% offset
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Yield	>= 455 MPa @Strain 0.200 %, Temperature 250 °C	>= 66000 psi @Strain 0.200 %, Temperature 482 °F
ThyssenKrupp N-A-XTRA® 550 Structural Steel This Material Specification applies to quenched and tempered heavy plates made of the special structural steel N-A-XTRA® This steel can be supplied in 3 different grades with a minimum yield streng..
Tensile Strength, Yield	455 MPa @Temperature 24.0 °C	66000 psi @Temperature 75.2 °F
Hexcel® F161 Epoxy Resin, 120 Glass Fabric Hexcel designation: 120-38"-F161; Fiber: 450-1/2Information provided by HexCel
Tensile Strength, Yield	455 MPa @Thickness >=508 mm	66000 psi @Thickness >=20.0 in	at center (L/T direction)
Alcoa QC-10® Aluminum Mold Alloy Specifically designed for high production injection and blow mold applications, QC-10 offers outstanding strength, stability, and durability. Its improved alloy composition provides outstanding, 1"-..
Tensile Strength, Yield	>= 455 MPa @Strain 0.200 %, Thickness 203.2 - 254 mm	>= 66000 psi @Strain 0.200 %, Thickness 8.000 - 10.0 in	Tempers T651 / T652
Constellium Alumold® 500 Rolled Aluminum The Alumold® 500 alloy has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important prop..
Tensile Strength, Yield	455 MPa @Strain 0.200 %, Thickness 140 - 160 mm	66000 psi @Strain 0.200 %, Thickness 5.51 - 6.30 in	Typical Strength
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m..
Tensile Strength, Yield	455 MPa @Strain 0.200 %	66000 psi @Strain 0.200 %	Typical
Aleris Hokotol Aluminum Alloy, 300 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..
Tensile Strength, Yield	>= 455 MPa @Thickness 3.17 mm	>= 66000 psi @Thickness 0.125 in	LT Direction
Alcoa 2090-T83 Aluminum Aluminum-lithium alloy developed for high strength aerospace applications. The Al-Cu-Li alloy offers an 8 per cent density savings when compared with other aerospace alloys. Alloy 2090-T83 also has ..
Tensile Strength, Yield	455 MPa @Temperature 149 °C	66000 psi @Temperature 300 °F	Annealed
ATI Wah Chang TI-3Al-2.5V Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..