Constellium Alumold® 500 Rolled Aluminum

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name Alumold®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium Alumold® 500 Rolled Aluminum.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Alumold® 500 alloy has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property for mould and tool construction. Typical applications include compression or injection moulds for plastics.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.82 g/cc
0.102 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 175

@Thickness 203.2 - 254 mm
 175

@Thickness 8.000 - 10.0 in
175

@Thickness 254 - 305 mm
 175

@Thickness 10.0 - 12.0 in
180

@Thickness 127 - 152.4 mm
 180

@Thickness 5.00 - 6.000 in
180

@Thickness 152.4 - 203.2 mm
 180

@Thickness 6.000 - 8.000 in
185

@Thickness 25.0 - 76.2 mm
 185

@Thickness 0.984 - 3.00 in
185

@Thickness 76.2 - 127 mm
 185

@Thickness 3.00 - 5.00 in
Tensile Strength >= 470 MPa

@Thickness 254 - 305 mm
 >= 68200 psi

@Thickness 10.0 - 12.0 in
 Tempers T651 / T652
>= 505 MPa

@Thickness 203.2 - 254 mm
 >= 73200 psi

@Thickness 8.000 - 10.0 in
 Tempers T651 / T652
510 MPa

@Thickness 254 - 305 mm
 74000 psi

@Thickness 10.0 - 12.0 in
 Typical Strength
>= 525 MPa

@Thickness 152.4 - 203.2 mm
 >= 76100 psi

@Thickness 6.000 - 8.000 in
 Tempers T651 / T652
535 MPa

@Thickness 203.2 - 254 mm
 77600 psi

@Thickness 8.000 - 10.0 in
 Typical Strength
>= 540 MPa

@Thickness 127 - 152.4 mm
 >= 78300 psi

@Thickness 5.00 - 6.000 in
 Tempers T651 / T652
>= 550 MPa

@Thickness 76.2 - 127 mm
 >= 79800 psi

@Thickness 3.00 - 5.00 in
 Tempers T651 / T652
555 MPa

@Thickness 152.4 - 203.2 mm
 80500 psi

@Thickness 6.000 - 8.000 in
 Typical Strength
>= 560 MPa

@Thickness 25.0 - 76.2 mm
 >= 81200 psi

@Thickness 0.984 - 3.00 in
 Tempers T651 / T652
570 MPa

@Thickness 127 - 152.4 mm
 82700 psi

@Thickness 5.00 - 6.000 in
 Typical Strength
580 MPa

@Thickness 76.2 - 127 mm
 84100 psi

@Thickness 3.00 - 5.00 in
 Typical Strength
590 MPa

@Thickness 25.0 - 76.2 mm
 85600 psi

@Thickness 0.984 - 3.00 in
 Typical Strength
Tensile Strength, Yield >= 435 MPa

@Strain 0.200 %,
Thickness 254 - 305 mm
 >= 63100 psi

@Strain 0.200 %,
Thickness 10.0 - 12.0 in
 Tempers T651 / T652
>= 455 MPa

@Strain 0.200 %,
Thickness 203.2 - 254 mm
 >= 66000 psi

@Strain 0.200 %,
Thickness 8.000 - 10.0 in
 Tempers T651 / T652
470 MPa

@Strain 0.200 %,
Thickness 254 - 305 mm
 68200 psi

@Strain 0.200 %,
Thickness 10.0 - 12.0 in
 Typical Strength
>= 472 MPa

@Strain 0.200 %,
Thickness 127 - 152.4 mm
 >= 68500 psi

@Strain 0.200 %,
Thickness 5.00 - 6.000 in
 Tempers T651 / T652
>= 473 MPa

@Strain 0.200 %,
Thickness 152.4 - 203.2 mm
 >= 68600 psi

@Strain 0.200 %,
Thickness 6.000 - 8.000 in
 Tempers T651 / T652
490 MPa

@Strain 0.200 %,
Thickness 203.2 - 254 mm
 71100 psi

@Strain 0.200 %,
Thickness 8.000 - 10.0 in
 Typical Strength
>= 497 MPa

@Strain 0.200 %,
Thickness 76.2 - 127 mm
 >= 72100 psi

@Strain 0.200 %,
Thickness 3.00 - 5.00 in
 Tempers T651 / T652
>= 504 MPa

@Strain 0.200 %,
Thickness 25.0 - 76.2 mm
 >= 73100 psi

@Strain 0.200 %,
Thickness 0.984 - 3.00 in
 Tempers T651 / T652
510 MPa

@Strain 0.200 %,
Thickness 152.4 - 203.2 mm
 74000 psi

@Strain 0.200 %,
Thickness 6.000 - 8.000 in
 Typical Strength
520 MPa

@Strain 0.200 %,
Thickness 127 - 152.4 mm
 75400 psi

@Strain 0.200 %,
Thickness 5.00 - 6.000 in
 Typical Strength
530 MPa

@Strain 0.200 %,
Thickness 76.2 - 127 mm
 76900 psi

@Strain 0.200 %,
Thickness 3.00 - 5.00 in
 Typical Strength
540 MPa

@Strain 0.200 %,
Thickness 25.0 - 76.2 mm
 78300 psi

@Strain 0.200 %,
Thickness 0.984 - 3.00 in
 Typical Strength
Elongation at Break >= 0.50 %

@Thickness 254 - 305 mm
 >= 0.50 %

@Thickness 10.0 - 12.0 in
 Tempers T651 / T652
>= 1.0 %

@Thickness 152.4 - 203.2 mm
 >= 1.0 %

@Thickness 6.000 - 8.000 in
 Tempers T651 / T652
>= 1.0 %

@Thickness 203.2 - 254 mm
 >= 1.0 %

@Thickness 8.000 - 10.0 in
 Tempers T651 / T652
1.5 %

@Thickness 203.2 - 254 mm
 1.5 %

@Thickness 8.000 - 10.0 in
 Typical Elongation
1.5 %

@Thickness 254 - 305 mm
 1.5 %

@Thickness 10.0 - 12.0 in
 Typical Elongation
2.0 %

@Thickness 152.4 - 203.2 mm
 2.0 %

@Thickness 6.000 - 8.000 in
 Typical Elongation
>= 2.5 %

@Thickness 127 - 152.4 mm
 >= 2.5 %

@Thickness 5.00 - 6.000 in
 Tempers T651 / T652
>= 4.0 %

@Thickness 76.2 - 127 mm
 >= 4.0 %

@Thickness 3.00 - 5.00 in
 Tempers T651 / T652
4.0 %

@Thickness 127 - 152.4 mm
 4.0 %

@Thickness 5.00 - 6.000 in
 Typical Elongation
>= 5.0 %

@Thickness 25.0 - 76.2 mm
 >= 5.0 %

@Thickness 0.984 - 3.00 in
 Tempers T651 / T652
6.0 %

@Thickness 76.2 - 127 mm
 6.0 %

@Thickness 3.00 - 5.00 in
 Typical Elongation
10 %

@Thickness 25.0 - 76.2 mm
 10 %

@Thickness 0.984 - 3.00 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
tensile
73.0 GPa
10600 ksi
compression
Poissons Ratio 0.33
0.33
Thermal Properties Metric English Comments
CTE, linear 23.7 µm/m-°C

@Temperature 20.0 - 100 °C
 13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Specific Heat Capacity 0.857 J/g-°C
0.205 BTU/lb-°F
Thermal Conductivity 153 W/m-K
1060 BTU-in/hr-ft²-°F
Descriptive Properties Value Comments
Thermal Diffusivity 63 mm²/s