Polymer Property : Tensile Strength, Yield = 36300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	250 MPa @Strain 1.00 %	36300 psi @Strain 1.00 %	EN min.,RT; EN 10002-1
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Yield	250 MPa @Strain 0.200 %	36300 psi @Strain 0.200 %	Outokumpu Typical,Cold Rolled Narrow Strip; EN 10002-1
Outokumpu 4303 Cr-Ni Austenitic Stainless Steel Good corrosion resistance with excellent drawing properties.Applications: Suitable for cold formed components where good workability is required. Fasteners, studs.Available in hot rolled plate (Qua..
Tensile Strength, Yield	250 MPa @Strain 0.200 %	36300 psi @Strain 0.200 %	EN min.,RT; EN 10002-1
Outokumpu 4310 Cr-Ni Austenitic Stainless Steel Cold work hardening steel suitable for manufacture of springs operating in corrosive conditions.Available hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and ro..
Tensile Strength, Yield	250 MPa @Strain 0.200 %	36300 psi @Strain 0.200 %	Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
Outokumpu 4541 Cr-Ni Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C..
Tensile Strength, Yield	250 MPa @Strain 0.200 %	36300 psi @Strain 0.200 %	Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
Outokumpu 4878 High Temperature Austenitic Stainless Steel Heat-resistant variant of 1.4541, with a slightly higher max carbon content. Recommended max service temperature for this steel in dry air is 800°C. Applications: Heat and creep resistance. For ..
Tensile Strength, Yield	>= 250 MPa @Strain 1.00 %	>= 36300 psi @Strain 1.00 %
Industeel CLC 18.15.4L 3% Mo Minimum Austenitic Stainless Steel Description: CLC 18-15-4L (317L) is an austenitic stainless steel with a 3% minimum Molybdenum addition. Alloys CLC 18-15-4L (317L) exhibit austenitic microstructure free of deleterious carbide prec..
Tensile Strength, Yield	>= 250 MPa @Strain 0.200 %, Thickness 12.5 - 40.0 mm	>= 36300 psi @Strain 0.200 %, Thickness 0.492 - 1.57 in	Temper T451; Standard EN 485-2
Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 2017A precision plates combine a very good dimensional stability with a high level of mechanical strength and elongation. The outstanding flatness, the low roughness and high quality of the..
Tensile Strength, Yield	250 MPa @Thickness 3.20 mm, Temperature 760 °C	36300 psi @Thickness 0.126 in, Temperature 1400 °F	0.2% offset
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Yield	250 MPa @Thickness 4.00 mm, Temperature 427 °C	36300 psi @Thickness 0.157 in, Temperature 801 °F	0.2% offset
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Yield	250 MPa @Strain 0.200 %	36300 psi @Strain 0.200 %	EN min.,RT; EN 10002-1
Outokumpu 725LN Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form.