Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides

Category Metal , Nonferrous Metal , Aluminum Alloy , 2000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name ALPLAN®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ALPLAN® 2017A precision plates combine a very good dimensional stability with a high level of mechanical strength and elongation. The outstanding flatness, the low roughness and high quality of the milled surfaces, protected by a plastic film, make surface milling by the end user superfluous. This combination of properties enables significant cost savings in machining. Applications include: reference plates, machine housings and lateral panels, transport tables, jigs.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.78 g/cc
0.100 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 125

@Thickness 7.90 - 25.0 mm
 125

@Thickness 0.311 - 0.984 in
125

@Thickness 25.0 - 60.0 mm
 125

@Thickness 0.984 - 2.36 in
125

@Thickness 60.0 - 155 mm
 125

@Thickness 2.36 - 6.10 in
Tensile Strength >= 370 MPa

@Thickness 60.0 - 80.0 mm
 >= 53700 psi

@Thickness 2.36 - 3.15 in
 Temper T451; Standard EN 485-2
>= 385 MPa

@Thickness 40.0 - 60.0 mm
 >= 55800 psi

@Thickness 1.57 - 2.36 in
 Temper T451; Standard EN 485-2
>= 390 MPa

@Thickness 7.90 - 12.5 mm
 >= 56600 psi

@Thickness 0.311 - 0.492 in
 Temper T451; Standard EN 485-2
>= 390 MPa

@Thickness 12.5 - 40.0 mm
 >= 56600 psi

@Thickness 0.492 - 1.57 in
 Temper T451; Standard EN 485-2
415 MPa

@Thickness 7.90 - 25.0 mm
 60200 psi

@Thickness 0.311 - 0.984 in
 Typical Strength; Standard EN 485-2
415 MPa

@Thickness 25.0 - 60.0 mm
 60200 psi

@Thickness 0.984 - 2.36 in
 Typical Strength; Standard EN 485-2
415 MPa

@Thickness 60.0 - 155 mm
 60200 psi

@Thickness 2.36 - 6.10 in
 Typical Strength; Standard EN 485-2
>= 495 MPa

@Thickness 80.0 - 115 mm
 >= 71800 psi

@Thickness 3.15 - 4.53 in
 Temper T451; Standard EN 485-2
Tensile Strength, Yield >= 240 MPa

@Strain 0.200 %,
Thickness 60.0 - 80.0 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 2.36 - 3.15 in
 Temper T451; Standard EN 485-2
>= 245 MPa

@Strain 0.200 %,
Thickness 40.0 - 60.0 mm
 >= 35500 psi

@Strain 0.200 %,
Thickness 1.57 - 2.36 in
 Temper T451; Standard EN 485-2
>= 250 MPa

@Strain 0.200 %,
Thickness 12.5 - 40.0 mm
 >= 36300 psi

@Strain 0.200 %,
Thickness 0.492 - 1.57 in
 Temper T451; Standard EN 485-2
>= 260 MPa

@Strain 0.200 %,
Thickness 7.90 - 12.5 mm
 >= 37700 psi

@Strain 0.200 %,
Thickness 0.311 - 0.492 in
 Temper T451; Standard EN 485-2
265 MPa

@Strain 0.200 %,
Thickness 25.0 - 60.0 mm
 38400 psi

@Strain 0.200 %,
Thickness 0.984 - 2.36 in
 Typical Strength; Standard EN 485-2
265 MPa

@Strain 0.200 %,
Thickness 60.0 - 155 mm
 38400 psi

@Strain 0.200 %,
Thickness 2.36 - 6.10 in
 Typical Strength; Standard EN 485-2
270 MPa

@Strain 0.200 %,
Thickness 7.90 - 25.0 mm
 39200 psi

@Strain 0.200 %,
Thickness 0.311 - 0.984 in
 Typical Strength; Standard EN 485-2
>= 420 MPa

@Strain 0.200 %,
Thickness 80.0 - 115 mm
 >= 60900 psi

@Strain 0.200 %,
Thickness 3.15 - 4.53 in
 Temper T451; Standard EN 485-2
Elongation at Break >= 6.0 %

@Thickness 80.0 - 115 mm
 >= 6.0 %

@Thickness 3.15 - 4.53 in
 Temper T451; Standard EN 485-2
>= 7.0 %

@Thickness 60.0 - 80.0 mm
 >= 7.0 %

@Thickness 2.36 - 3.15 in
 Temper T451; Standard EN 485-2
>= 12 %

@Thickness 12.5 - 40.0 mm
 >= 12 %

@Thickness 0.492 - 1.57 in
 Temper T451; Standard EN 485-2
>= 12 %

@Thickness 40.0 - 60.0 mm
 >= 12 %

@Thickness 1.57 - 2.36 in
 Temper T451; Standard EN 485-2
>= 13 %

@Thickness 7.90 - 12.5 mm
 >= 13 %

@Thickness 0.311 - 0.492 in
 Temper T451; Standard EN 485-2
17 %

@Thickness 60.0 - 155 mm
 17 %

@Thickness 2.36 - 6.10 in
 Typical Elongation
20 %

@Thickness 7.90 - 25.0 mm
 20 %

@Thickness 0.311 - 0.984 in
 Typical Elongation
20 %

@Thickness 25.0 - 60.0 mm
 20 %

@Thickness 0.984 - 2.36 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
Thermal Properties Metric English Comments
CTE, linear 23.6 µm/m-°C

@Temperature 20.0 - 100 °C
 13.1 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 125 - 140 W/m-K
868 - 972 BTU-in/hr-ft²-°F
Temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 91.4 - 95.5 %
91.4 - 95.5 %
as balance
Chromium, Cr <= 0.10 %
<= 0.10 %
Copper, Cu 3.5 - 4.5 %
3.5 - 4.5 %
Iron, Fe <= 0.70 %
<= 0.70 %
Magnesium, Mg 0.40 - 1.0 %
0.40 - 1.0 %
Manganese, Mn 0.40 - 1.0 %
0.40 - 1.0 %
Silicon, Si 0.20 - 0.80 %
0.20 - 0.80 %
Zinc, Zn <= 0.25 %
<= 0.25 %
Zr+Ti <= 0.25 %
<= 0.25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000360 - 0.00000420 ohm-cm
0.00000360 - 0.00000420 ohm-cm
Temper T651