Polymer Property : Tensile Strength, Yield = 13000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	LW; ASTM D638
Industrial Laminates/Norplex NP320E Cotton Fabric Description: Similar to NP320 with improved moisture resistance. Suitable for electrical applications in moderate humidity conditions.Thickness Tested: 0.062", 0.125", and 0.500â€
Tensile Strength, Yield	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	LW; ASTM D638
Industrial Laminates/Norplex NP320U Cotton Fabric Description: Utility version of NP320E. Meets most, but not all, NEMA properties for L and LE, and is not certifiable as a NEMA Grade.Thickness Tested: 0.062", 0.125", and 0.500"
Tensile Strength, Yield	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	CW; ASTM D638
Industrial Laminates/Norplex NP600 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is most commonly used for drill entry material in the PCB industry. Thickness Tested: 0.062"..
Tensile Strength, Yield	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	CW; ASTM D638
Industrial Laminates/Norplex NP602 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. It is typically hot punched for numerous low voltage, less than 250 volts, electrical applications.Thickne..
Tensile Strength, Yield	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	CW; ASTM D638
Industrial Laminates/Norplex NP605 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is normally used in the printed circuit board industry as a backup for the drilling operatio..
Tensile Strength, Yield	89.6 MPa @Strain 0.0800 %, Temperature 1000 °C	13000 psi @Strain 0.0800 %, Temperature 1830 °F
COI Ceramics Sylramic™ S200 Silicon Carbide Ceramic Matrix Composite, CG Nicalon Engineered ceramic composite structure.Reinforcing Fiber Flexibility: S400 - Carbon Preceramic Polymer Matrix Precursors: S400 - Crystalline (SiC + Si3N4) or SiCPhysical Attributes: Dense Matrix (