Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Izod Impact, Notched (ISO) | 1.50 kJ/m² @Thickness 4.00 mm, Temperature -30.0 °C |
0.714 ft-lb/in² @Thickness 0.157 in, Temperature -22.0 °F |
ISO 180/1A |
Polimeri Europa Edistir N 1782 Polystyrene General purpose polystyrene with good flow and high heat resistance. Suggested for direct gassing extrusion of heavy gage insulating boards (XPS) and in blend with high concentration of clear SBS f.. |
|||
Izod Impact, Notched (ISO) | 1.50 kJ/m² @Thickness 4.00 mm, Temperature -30.0 °C |
0.714 ft-lb/in² @Thickness 0.157 in, Temperature -22.0 °F |
ISO 180/1A |
Polimeri Europa Edistir N 1840 Polystyrene General purpose polystyrene combining easy flow and medium heat. Edistir N 1840 is suggested in extrusion for glossy capping of HIPS sheets and for blending with HIPS or clear SBS for stiffer therm.. |
|||
Izod Impact, Notched (ISO) | 1.50 kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C |
0.714 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
Premix Thermoplastics PRE-ELEC® PP 1394 Conductive Thermoplastic Compound PRE-ELEC® PP 1394 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Izod Impact, Notched (ISO) | 1.50 kJ/m² @Temperature 0.000 °C |
0.714 ft-lb/in² @Temperature 32.0 °F |
ISO 180 |
LyondellBasell Hostacomâ„¢ TKS709D Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ TKS709D medium high melt flow, 1,600 MPa flexural modulus, UV-stabilized, thermoplastic elastomeric olefin (TEO) resin has an excellent combination of properties and proc.. |
|||
Izod Impact, Notched (ISO) | 1.50 kJ/m² @Thickness 4.00 mm, Temperature -30.0 °C |
0.714 ft-lb/in² @Thickness 0.157 in, Temperature -22.0 °F |
ISO 180/1A |
Polimeri Europa Edistir N 1910 Polystyrene Very easy flow general purpose polystyrene. Used for injection of thin-wall, multi-cavity, very fast-cycle mouldings and for sheet extrusion in glossy capping of HIPS and in blend with HIPS or clear.. |