Polimeri Europa Edistir N 1840 Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Edistir
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Edistir N 1840 Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose polystyrene combining easy flow and medium heat. Edistir N 1840 is suggested in extrusion for glossy capping of HIPS sheets and for blending with HIPS or clear SBS for stiffer thermoformable sheets. This grade exhibits excellent processability in injection moulding and it is recommended for complex and thin-wall parts and fast moulding cycles. Designation: Thermoplastics ISO 1622-PS,G,085-12Applications: Thermoformed disposable packaging and glossy sheets for industrial and fridge applications. Injection moulded beverage cups, point of sales, containers for foods and cosmetics, toys, housewares, medical articles (Petri dishes).Edistir N 1840 is certified UL94 HB "all colors" at 1.5 mm (UL file E83071). This grade in its natural version complies by composition with the requirements set by the main Regulations for plastic materials intended for food contact (including the EEC Directive 90/128 and subsequent amendments).Information provided by Polimeri Europa
Physical Properties Metric English Comments
Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
24 hours - 23°C; ISO 62
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Internal Method
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 200 °C
10 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80
80
ISO 2039/2
Tensile Strength at Break 39.0 MPa
5660 psi
5 mm/min; ISO 527
Elongation at Break 1.8 %
1.8 %
5 mm/min; ISO 527
Tensile Modulus 3.25 GPa
471 ksi
1 mm/min; ISO 527
Flexural Strength 69.0 MPa
10000 psi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 1.50 kJ/m²

@Thickness 4.00 mm,
Temperature -30.0 °C
0.714 ft-lb/in²

@Thickness 0.157 in,
Temperature -22.0 °F
ISO 180/1A
1.70 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
0.809 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
120°C/h; ASTM D 648
Vicat Softening Point 88.0 °C
190 °F
50 N - 50°C/h; ISO 306/B
92.0 °C
198 °F
10 N - 50°C/h; ISO 306/A
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+15 ohm-cm
7.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.50e+15 ohm
1.50e+15 ohm
IEC 60093
Dielectric Constant 2.5

@Frequency 50 Hz
2.5

@Frequency 50 Hz
IEC 60250
Dielectric Strength 70.0 kV/mm
1780 kV/in
IEC 60243
Dissipation Factor 0.00020

@Frequency 50 Hz
0.00020

@Frequency 50 Hz
IEC 60250
Comparative Tracking Index 375 V
375 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 210 - 240 °C
410 - 464 °F
Extrusion
200 - 250 °C
392 - 482 °F
Injection Molding
Mold Temperature 10.0 - 50.0 °C
50.0 - 122 °F
Injection Molding