- Polymer Property : Tensile Strength at Break = 4.00 MPa
Polymer Property : Tensile Strength at Break = 4.00 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 4.00 MPa | 580 psi | ISO 37 |
| PolyOne OnFlex™ S EH 40A-3S7001 Thermoplastic Elastomer (TPE) OnFlex™ S EH thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are formulated to deliver a great cost/performance ratio in addition to t.. |
|||
| Tensile Strength at Break | 4.00 MPa @Temperature 23.0 °C |
580 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
| PolyOne Versaflex™ OM 6275-1 Thermoplastic Elastomer (TPE) Versaflex™ OM 6275-1 is specifically designed to bond to a variety of standard and modified nylon materials, including those which are glass-filled, heat stabilized and/or impact modified. New Prod.. |
|||
| Tensile Strength at Break | 4.00 MPa @Temperature 23.0 °C |
580 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
| PolyOne Versalloy™ HC 9210-55N Thermoplastic Elastomer (TPE) Versalloy™ HC 9210-55N is a TPV alloy targeted for injection molding healthcare applications such as disposable medical items, syringe stoppers, and soft-touch overmolding onto surgical grips. Prod.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ASTM D412 |
| Polimeri Europa Europrene® SOL T 6205 Styrene - Butadiene Block Copolymer Europrene® SOL T 6205 is a radial block copolymer obtained by anionic polymerization. The polymer is based on styrene and butadiene, where bound styrene is 25% weight and diblock content is 15%. .. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ASTM D412 |
| Polimeri Europa Europrene® SOL T 9133 Styrene - Isoprene Block Copolymer Europrene® SOL T 9133 is a linear block copolymer obtained by anionic polymerization. The polymer is based on styrene and isoprene, where bound styrene content is 16% weight and diblock content is.. |
|||
| Tensile Strength at Break | 4.00 - 8.00 MPa | 580 - 1160 psi | ASTM D412 |
| Proto3000 Objet Digital Materials™ DM_9885/9785 Rubber-like Prototyping Polymer Primary material: TangoBlackPlus/TangoPlusSecondary material: VeroWhitePlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structu.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL WCP700 PPE-TPE Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL WCP700 PPE-TPE (Asia Pacific) Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | Die C; Cross direction; ASTM D412 |
| Teknor Apex Sarlink® 4145 Thermoplastic Elastomer A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® 4145 is a low hardness grade possessing exceptional tensile strength, superior compression set, chemical re.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ASTM D638 |
| ELASTO UK Dryflex® 500350S SEBS Based Material, Unfilled Qualities, 35A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ASTM D638 |
| ELASTO UK Dryflex® 502350S SEBS Based Material, Unfilled Qualities, 35A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
| Tensile Strength at Break | >= 4.00 MPa | >= 580 psi | (20 in/min), Molded Properties; ASTM D638 |
| ExxonMobil Escorene™ UL 04533EH2 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 04533EH2 is a copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Fre.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | Across Flow; ASTM D412 |
| ExxonMobil Santoprene® 121-50E500 Thermoplastic Elastomer A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material has controlled rheology for robotic or specialty extrusion applications. This g.. |
|||
| Tensile Strength at Break | >= 4.00 MPa | >= 580 psi | ISO R 527 |
| Fainplast Compounds CRKA 78 Flexible PVC, Flame Retardant Electrical Bedding Lead Free Flame retardant bedding |
|||
| Tensile Strength at Break | >= 4.00 MPa | >= 580 psi | ISO 527 |
| Fainplast Compounds EVAtech 805S Ethylene Vinyl Acetate Foam EVA (ethylene-vinyl acetate) designed for the production of crosslinked expanded products using injection technology.Information provided by Fainplast Compounds |
|||
| Tensile Strength at Break | >= 4.00 MPa | >= 580 psi | ISO R 527 |
| Fainplast Compounds CRKA 90 Flexible PVC, Flame Retardant Electrical Bedding Lead Free Bedding non contaminating on XLPE |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ISO R 527 |
| Fainplast Compounds GS 30 Flexible PVC, Injection Molding, Lead Free Scooter handle-bar grip |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | |
| Beijing Evergrow Resources GFF-3 Glass Fiber Felt Introduction:By applying high-count fiberglass, GFNF series has the excellent properties such as heat-isolation, fire-resistance, anti-corrosion and heat-preservation. It's the most characteristic a.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ASTM D638 |
| Arkema Group LOTADER® AX 8900 Terpolymer Ethylene - Acrylic Ester - Glycidyl Methacrylate LOTADER® AX 8900 is a random terpolymer of ethylene, acrylic ester and glycidyl methacrylate, polymerized under high pressure in an autoclave process. Comonomer content is high. Due to its properti.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ASTM D412 |
| 3M 560 Polyurethane Adhesive Sealant 3M™ 500-Series Polyurethane Construction Sealant, Polyurethane Sealant and Polyurethane Adhesive Sealant products are one component, moisture curing products which form permanent elastic bonds. The.. |
|||
| Tensile Strength at Break | 4.00 MPa | 580 psi | ISO 527-1 |
| Barlog Plastics KEBAFLEX E 50.1 TPE-V, Shore A50 TPE-VInformation provided by BARLOG plastics GmbH. |
|||