Polymer Property : Tensile Strength at Break = 31.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.7 MPa
4600 psi
2 in/min; ASTM D638
RheTech Products M15P101-01A 15% Mica Reinforced Polypropylene, Black
Applications: Air ducts - distributionFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 31.7 MPa
4600 psi
2 in/min; ASTM D638
RheTech Products T10P102-00EG 10% Talc Reinforced Polypropylene, Extrusion Grade, Natural
Injection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D638
LyondellBasell Petrothene® KR92828 High Density Polyethylene
ApplicationsPETROTHENE KR 92828 is a high molecular weight, high density polyethylene-based compound designed for use in jacketing, conduit or wire insulation. KR 92828 contains a carbon black cont..
Tensile Strength at Break 31.7 MPa
4600 psi
after 16 hours in 50°C water
Malvern Minerals Nylon with Novacite® L-337 Quartz Filler
Product data demonstrates the effect of the Novacite® (untreated lamellar quartz) filler. A separate entry demonstrates the effect of treated Novakup® filler in nylon. The specific nylon use..
Tensile Strength at Break 31.7 MPa
4600 psi
at max load; ASTM D638
A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
DescriptionPolypropylene PP 1667-01 is an easy flowing natural homopolymer polypropylene. It is for injection molding large parts with thin sections requiring good stiffness, heat resistance, and c..
Tensile Strength at Break 31.7 MPa
4600 psi
at max load; ASTM D638
A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
DescriptionPolypropylene PP 1667-01 is an easy flowing natural homopolymer polypropylene. It is for injection molding large parts with thin sections requiring good stiffness, heat resistance, and c..
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D 638
RTP Company ESD C 705 High Density Polyethylene (HDPE), Glass Fiber - Electrically Conductive - ESD Protection
Tensile Strength at Break 31.7 MPa
4600 psi
at max load; ASTM D638
A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
DescriptionPolypropylene PP 1667-01 is an easy flowing natural homopolymer polypropylene. It is for injection molding large parts with thin sections requiring good stiffness, heat resistance, and c..
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D 638
RTP Company RTP 132 Polypropylene (PP), Talc
Tensile Strength at Break 31.7 MPa
4600 psi
at max load; ASTM D638
A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
DescriptionPolypropylene PP 1667-01 is an easy flowing natural homopolymer polypropylene. It is for injection molding large parts with thin sections requiring good stiffness, heat resistance, and c..
Tensile Strength at Break 31.7 MPa
4600 psi
at max load; ASTM D638
A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
DescriptionPolypropylene PP 1667-01 is an easy flowing natural homopolymer polypropylene. It is for injection molding large parts with thin sections requiring good stiffness, heat resistance, and c..
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D 638
RTP Company RTP 2099 X 124790 F Bio-Based Polylactic Acid (PLA); Impact Modified - Mineral - Fast-Cycle Nucleator - 53% Renewable Resource Content
Nucleated for high heat exposure.  For detailed processing information regarding this, see the PLA Molding Guide on the RTP Company website.
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D638
Eastman Tenite 360E4861314 Cellulose Acetate Propionate, Clear, Trsp
Applications:ProfilesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. T..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 15 s set time
Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 50 s set time
Elmer's Products Aron Alpha® 202 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 5 s set time
Elmer's Products Aron Alpha® 202F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 15 s set time
Elmer's Products Aron Alpha® 212E Cyanoacrylate Adhesive (Industrial Krazy Glue™)
For clean, fast applications. Best for high speed automated assembly.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous s..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 10 s set time
Elmer's Products Aron Alpha® 221 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 3 s set time
Elmer's Products Aron Alpha® 221F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 3 s set time
Elmer's Products Aron Alpha® 231F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 15 s set time
Elmer's Products Aron Alpha® 232 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 15 s set time
Elmer's Products Aron Alpha® 253TX Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 15 s set time
Elmer's Products Aron Alpha® 282F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4600 psi
Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Dow DGDA-2475 NT High Density Polyethylene Resin
DOW DGDA-2475 NT is produced using UNIPOL™ process technology. It is intended for use in corrugated pipe applications. It has been specifically designed for extrusion of corrugated pipes with the..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 40 s set time
Elmer's Products Aron Alpha® 241 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 15 s set time
Elmer's Products Aron Alpha® 241E Cyanoacrylate Adhesive (Industrial Krazy Glue™)
For clean, fast applications. Best for high speed automated assembly.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous subs..
Tensile Strength at Break 31.7 MPa
4600 psi
vs. steel; 10 s set time
Elmer's Products Aron Alpha® 252F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break 31.7 MPa
4590 psi
ASTM D3759
3M Scotch® 234 General Purpose Masking Tape
Scotch® General Purpose Masking Tape 234 is designed to be used in medium temperature paint bake operations.Information provided by 3M
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D 638
RTP Company RTP 132 Z Polypropylene (PP), Mineral - FDA Compliant Ingredients
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D 638
RTP Company RTP 142 Polypropylene (PP), Calcium Carbonate