Polymer Property : Tensile Strength at Break = 31.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	31.4 MPa	4550 psi
Indium Corp. Indalloy 23 Bismuth Solder Alloy Non-electrical solder for low-ambient temperatureInformation Provided by Indium Corporation
Tensile Strength at Break	31.4 MPa	4560 psi	ASTM D 638
Shakespeare Isocorâ„¢ HG20SC Nylon 612 Isocorâ„¢ HG20SC us a medium viscosity compounding grad PA-612 based nylon. This resin is specifically suited for applications requiring lower moisture regain and greater dimensional stability...
Tensile Strength at Break	31.4 MPa	4560 psi	ASTM D 638
Shakespeare Isocorâ„¢ HG26SI medium viscosity PA-612 Isocorâ„¢ HG26SI is a medium viscosity PA-612 based nylon. This resin is specifically suited for applications requiring low moisture regain and greater dimensional stability. Isocorâ„¢ HG2..
Tensile Strength at Break	31.4 MPa	4550 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SD-0150UF ABS, Unreinforced Information provided by Samsung Cheil Industries.
Tensile Strength at Break	31.4 MPa	4550 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VH-0819 ABS, Unreinforced FR Flame-retardant high flow ABS that can be used for the exterior of large TV and OA devicesInformation provided by Samsung Cheil Industries.
Tensile Strength at Break	31.4 MPa	4550 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SD-0150UF ABS, Unreinforced Information provided by Samsung Cheil Industries.
Tensile Strength at Break	31.4 MPa	4550 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VH-0819 ABS, Unreinforced FR Flame-retardant high flow ABS that can be used for the exterior of large TV and OA devicesInformation provided by Samsung Cheil Industries.
Tensile Strength at Break	31.4 MPa	4550 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 515 Flame Retardant Polystyrene Characteristics Good flow properties Good balance of toughness and rigidity Available in any colorProcessing Injection molding Extrusion Applications Electrical switch boards MCB distribution bo..
Tensile Strength at Break	31.4 MPa	4550 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 6410 0003 Abrasion Resistant Polystyrene Characteristics Self lubricating, abrasion resistant Low specific Gravity Suitable for multicavity thin wall parts Excellent thermal stability and easy to color Processing Injection moldingApplic..
Tensile Strength at Break	31.4 MPa	4550 psi	ASTM D638
Toyobo PELPRENE™ P90BD Polyester TPE, High Viscous, High Durability Features: Polyester TPE, High Viscous, High DurabilityInformation provided by Toyobo.
Tensile Strength at Break	31.4 MPa	4550 psi	ASTM D638
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It ..
Tensile Strength at Break	31.4 MPa	4550 psi	ASTM D638
Unitika elitel UE3500 Polyester, Flake High molecular weight, High toughness, High strength, High elongationUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from produc..
Tensile Strength at Break	31.4 MPa	4550 psi	50 mm/min; ASTM D638
Supreme Petrochem SP6409 High Gloss Polystyrene Characteristics High gloss in co-extrusion Improved dart impact strength of co-extruded sheets Processing Co-extrusion cap layer Applications Gloss cap layer for refrigerator liner and other formin..