- Polymer Property : Tensile Strength at Break = 28300 psi
Polymer Property : Tensile Strength at Break = 28300 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 195 MPa | <= 28300 psi | ISO/R527 |
| Polykemi AB SCANAMID 66 A12^ F35 Nylon 66, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | 10mm/min; ASTM D638 |
| Kingfa PA6-G50 50% Glass Fiber Reinforced PA6 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 218G1 V30 Black 34N PA66, 30% glass fiber, DRY Description: Polyamide 66, reinforced with 30% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. For 7.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 218G2 V30 Black 34N PA66, 30% glass fiber, DRY Description: TECHNYL® A 218G2 V30 Black 34N is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. The product is available in black color. Benefits: This .. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Solvay TECHNYL® C 216 V35 Black Z PA6, 35% glass fiber, DRY Description: Polyamide PA6 , reinforced with 35 % of glass fiber, for injection molding.Available in: North AmericaProduct Applications: It has good mechanical properties, it is used in all sectors .. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Solvay TECHNYLSTARâ„¢ AFX 218 V60 PA6, 60% glass filled, Conditioned Description: TECHNYLSTARâ„¢ AFX 218 V60 is based on a patented high flow polyamide 66 resin (Technylstar), heat stabilized, reinforced with 60% of glass fiber, for injection molding.Benefits: Due.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Solvay TECHNYLSTARâ„¢ S 216 V35 PA6, 35% glass filled, DRY Description: TECHNYLSTAR polyamide, reinforced with 35% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Europe and North AmericaProduct Applications.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP RF007SXQ PA 66 LNP THERMOCOMP* RF007SXQ is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Hydrolysis Resistant. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 216 V33 PA66, 33% glass fiber, DRY Description: TECHNYL® A 216 V33 is a polyamide 66, reinforced with 33% of glass fiber, for injection molding. This product is available in natural color.Benefits: The product offers an excellent .. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-93 |
| Wellman Wellamid® GF1398-N1 30% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1/-2 |
| DSM Akulon® K224-HG7 (Dry) 35% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1/-2 |
| DSM Akulon® K224-HG7 Nylon 6-35% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® AG-30 H PA66 Product description: Grilon AG-30 H black 9836 is a normal viscosity, specially heat stabilized PA 66 injection molding grade with 30% glass fibres. Grilon AG-30 H black 9836 has the following impor.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 |
| Eurotec® Tecomid® NB40 GR40 NL PA 6 40% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | 0.2 in/min; ASTM Test |
| BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® R530H BK0201 Nylon 66, 30% Glass Reinforced, DAM Vydyne® R530H BK0201 is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in black, it is specifically designed to maximize the retention of p.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® R530H BK0202 Nylon 66, 30% Glass Reinforced, DAM Vydyne® R530H BK0202 is general-purpose, recycled, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in black, it is specifically designed to maximize the rete.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1/-2 |
| BASF Ultramid® B3EG7 35% Glass Filled PA6 (Dry) Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1/-2 |
| BASF Ultramid® B3EG7 BK 00564 35% Glass Filled PA6 (Dry) Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO R 527 |
| Addiplast Addinyl C2 V40 Nylon 66/6, 40% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | |
| Radici Radilon® A RV350 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | |
| Radici Radilon® A RV400 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO R 527 |
| Addiplast Addinyl C2 ZV40 Nylon 66/6, 40% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |
|||