- Wellman Wellamid® GF1398-N1 30% Glass Fiber Reinforced Nylon 66
Wellman Wellamid® GF1398-N1 30% Glass Fiber Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® GF1398-N1 30% Glass Fiber Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183-87 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-93 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-93 |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178-93 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 12.5 kJ/m² | 5.95 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-93 |