Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	15.5 MPa	2250 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R4510H Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	15.5 MPa	2250 psi	ISO R 527
Stir SpA G MORBIDO (PVC) Application: Extrusion for refrigerator sealsInformation provided by STIR SpA
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D638
Teknor Apex APEXÂ® 3300-75NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Ethylene Oxide Sterilizable Uses: Food Service Application; Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tek..
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D638
Teknor Apex APEXÂ® 7500-80 Polyvinyl Chloride, Flexible Notes: 105Â°C General Purpose; RoHS Compliant Features: High Heat Resistance Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL..
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D638
Teknor Apex APEXÂ® 01-A0087A-91 Polyvinyl Chloride, Flexible Notes: 75Â°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D638
Teknor Apex APEXÂ® 3300R-75NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D412
Teknor Apex MF 170 NT Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsAppearance-ClearInformation provided by Teknor Apex Company
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D412
Teknor Apex Telcar® TL-1934A BLK 111 Thermoplastic Elastomer Information Provided by Teknor Apex
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D638
ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin Escorene Ultra LD 705.MJ is a fraction melt index, 13.3 wt% vinyl acetate copolymer suitable for use in making blow molded articles, extruded profiles and compounds.Information provided by ExxonMobi..
Tensile Strength at Break	15.5 MPa	2250 psi	Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Dow FINGERPRINT™ DFDA-7510 NT Linear Low Density Polyethylene Resin FINGERPRINT™ DFDA-7510 NT resin is produced using UNIPOL™ process technology. It is intended for use in micro irrigation tube, durable hose and tube, profile extrusion, and injection molded fitti..
Tensile Strength at Break	15.5 MPa	2250 psi	Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Dow DNDB-7441 NT 7 Linear Low Density Polyethylene Resin DOW DNDB-7441 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in hose and tube applications. It also has utility in gasketing, spiral wound hose, and corrugated hose ..
Tensile Strength at Break	15.5 MPa	2250 psi	ISO 37
Alliance Polymers Viprene™ P45D-22U-BLK Thermoplastic Vulcanizate Elastomer Viprene™ P45D-22U-BLK is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac..
Tensile Strength at Break	15.5 MPa	2250 psi	Transverse; ASTM D3759
3M ScotchPad™ 3750P Tape Pad 3M™ ScotchPad™ Tape Pad 3750P is a pre-cut pad formed with layered, high-performance tape sheets featuring durable 3M™Scotchpro™ film backing that is strong, conformable, and resistant to impact..
Tensile Strength at Break	15.5 MPa	2250 psi	Transverse; ASTM D3759
3M ScotchPad™ 809G Custom Tape Pads 3M™ ScotchPad™ Custom Tape Pad 809G is a pre-cut pad formed with layered, high performance tape sheets featuring durable 3M™ Scotchpro™ film backing that is strong, conformable and resistant to ..
Tensile Strength at Break	15.5 MPa	2250 psi	Transverse; ASTM D3759
3M ScotchPad™ 822 Label Protection Tape Pad 3M™ ScotchPad™ Label Protection Tape Pad 822 is a pre-cut pad formed with layered high-performance tape sheets featuring durable 3M™ ScotchPad™ polypropylene film backing that is strong, conform..
Tensile Strength at Break	15.5 MPa	2250 psi	ISO 37
Alliance Polymers Viprene™ P45D-22U-NAT Thermoplastic Vulcanizate Elastomer Viprene™ P45D-22U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac..
Tensile Strength at Break	15.5 MPa	2250 psi	ASTM D638
Resirene Resirene® 2210 High Impact Polystyrene Features:Very High FlowEasy ProcessingGood GlossFlexibilityFDA Rating: 21 CFR 177.1640High ProductivityApplications:InjectionThin Wall ApplicationsHard to Fill MoldsTelephonical DevicesYot CupsToysC..