Polymer Property : Tensile Strength at Break = 1960 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.5 MPa	1960 psi	ASTM D638
Petroquimica Triunfo Trithene® TX 8024 LDPE - High Clarity Film The Trithene TX 8024 resin is a low-density polyethylene (LDPE) with high molecular weight and distribution narrow, designed to obtain films with very high clarity and excellent processability. This..
Tensile Strength at Break	13.5 MPa @Temperature 110 Â°C, Time 1.21e+6 sec	1960 psi @Temperature 230 Â°F, Time 336 hour	500mm/min; ASTM D638
LG Chemical LUTENE CCO550BK PE Compound Description: LUTENE CC0550BK offer the following properties: high mechanical properties, good environmental stress cracking resistance, excellent wetherability and high speed extrusion to give a smo..
Tensile Strength at Break	13.5 MPa	1960 psi	ISO R 527
Stir SpA SG 55 ATC (PVC) Application: Extrusion non-toxic seal for wood window and door framesInformation provided by STIR SpA
Tensile Strength at Break	13.5 MPa	1960 psi	ISO R 527
Stir SpA SR 70 (PVC) Application: Extrusion sheath with good flexibility type TM-2Cold flex = -33Â°CInformation provided by STIR SpA
Tensile Strength at Break	13.5 MPa	1960 psi	ASTM D412
Teknor Apex Telcar® TL-8712 Thermoplastic Elastomer Notes: RoHS Compliant Uses: Appliance Wire Insulation; Appliance Wire Jacketing; Cable Jacketing; Connectors; Flexible Cord Jacketing; Industrial Cable Jacketing; Terminal Cable Jacketing; Undergrou..
Tensile Strength at Break	>= 13.5 MPa	>= 1960 psi	after aging (168h, 136°C); ASTM D638
Borealis LR4201R Polyethylene Insulation Compound, Crosslinkable LR4201R is a natural low-density crosslinkable polyethylene compound. Applications: LR4201R is intended for insulation of XLPE power cables with rated voltages up to 72 kV. Specifications: ISO 1872..
Tensile Strength at Break	13.5 MPa	1960 psi	after crosslinking process; IEC 60811
Fainplast Compounds HAX HFX 024-21L Halogen Free PVC This product is a LSFOH silane grafted compound for cable insulation and sheating, cross-linking by heat and moisture by previous addition of a suitable catalyst masterbatch. It is highly recommende..
Tensile Strength at Break	13.5 MPa	1960 psi	ASTM D3759
3M 483 Polyethylene Tape 3M™ Polyethylene Tape 483 has a polyethylene backing with a rubber adhesive for many general purpose applications including sealing, color coding, protecting, moisture proofing. Black tape has exce..
Tensile Strength at Break	13.5 MPa	1960 psi	ASTM D638
IRPC Polimaxx Polene V1160 High Density Polyethylene CHARACTERISTICS: GOOD FLOWABILITYAPPLICATIONS: INJECTION MOLDING FOR LIGHT WEIGHT HOUSEHOLDS, TOYS, FOOD CONTAINERS, COSMETICS CLOSURES, DISPOSABLE ARTICLES, LARGE MOLDING AND COMPLICATED PARTS