Polymer Property : Tensile Strength at Break = 151 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	151 MPa	21900 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 LNP* LUBRICOMP* RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Tensile Strength at Break	151 MPa	21900 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 (Asia Pacific) LNP* Lubricomp* RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Strength at Break	151 MPa	21900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9200 PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Strength at Break	151 MPa	21900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Strength at Break	151 MPa	21900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66 LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding.
Tensile Strength at Break	151 MPa	21900 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead.
Tensile Strength at Break	151 MPa	21900 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 (Asia Pacific) LNP* Thermocomp* RFB66 is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass.
Tensile Strength at Break	151 MPa	21900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WC006 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber.
Tensile Strength at Break	151 MPa	21900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp LF004 PEEK LNP THERMOCOMP* LF004 is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.