SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.340 % | 0.340 % | 50% RH, 24 hrs; ASTM D570 |
| 0.510 % | 0.510 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 122 MPa | 17700 psi | 5 mm/min; ISO 527 |
| 138 MPa | 20000 psi | Type I, 5 mm/min; ASTM D638 | |
| 151 MPa | 21900 psi | ASTM D638 | |
| Tensile Strength, Yield | 128 MPa | 18600 psi | 5 mm/min; ISO 527 |
| 138 MPa | 20000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| 1.7 % | 1.7 % | 5 mm/min; ISO 527 | |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.36 GPa | 1938 ksi | 1 mm/min; ISO 527 |
| 14.98 GPa | 2173 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
| 221 MPa | 32100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 248 MPa | 36000 psi | ASTM D790 | |
| Flexural Yield Strength | 222 MPa | 32200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 12.57 GPa | 1823 ksi | 2 mm/min; ISO 178 |
| 13.0 GPa | 1890 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 13.78 GPa | 1999 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.630 J/cm | 1.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.32 J/cm | 9.97 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 244 °C @Thickness 3.20 mm |
471 °F @Thickness 0.126 in |
unannealed; ASTM D648 |