Polymer Property : Tensile Strength at Break = 15.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	15.4 MPa	2230 psi	ASTM D638
Teknor Apex APEXÂ® 536 Polyvinyl Chloride, Flexible Notes: 60Â°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molde..
Tensile Strength at Break	15.4 MPa	2240 psi	ASTM D638
Teknor Apex APEXÂ® 327 Polyvinyl Chloride, Flexible Notes: 60Â°C Insulation; RoHS Compliant Uses: Flexible Cord Insulation; Flexible Cord JacketingForms: Pellets Wire Types: SJT; SPT-1; SPT-2; SPT-3; SRDT; ST; SVT Agency Ratings: UL 1581; UL 62 Pro..
Tensile Strength at Break	15.4 MPa	2240 psi	ASTM D638
Teknor Apex APEXÂ® 6500-75 Polyvinyl Chloride, Flexible Notes: 60Â°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molde..
Tensile Strength at Break	15.4 MPa	2230 psi
ExxonMobil LL 5252.09 Compounding Resin Product Description: LL 5252.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. The granular from of LL 5252.09 makes for efficient blending ..
Tensile Strength at Break	15.4 MPa	2240 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FE 5620Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5620Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..
Tensile Strength at Break	15.4 MPa	2240 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FE 5621 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5621 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul..