BASF Ultramid® 8202 PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8202 PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ultramid 8202 HS) and/or pigmented versions. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance.
Physical Properties Metric English Comments
Density 0.932 g/cc
0.0337 lb/in³
Melt; ISO 1183
1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 1.6 %
1.6 %
24 hour; ISO Test
9.5 %
9.5 %
ISO 62
Moisture Absorption at Equilibrium 2.7 %
2.7 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 48
48
Formic Acid
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM Test
Tensile Strength at Break 75.0 MPa
10900 psi
0.2 in/min; ASTM Test
Tensile Strength, Yield 78.0 MPa
11300 psi
50mm/min; ISO 527
79.0 MPa
11500 psi
2 in/min; ASTM Test
25.0 MPa

@Temperature 120 °C
3630 psi

@Temperature 248 °F
ISO Data
25.0 MPa

@Temperature 120 °C
3630 psi

@Temperature 248 °F
ASTM Test
35.0 MPa

@Temperature 80.0 °C
5080 psi

@Temperature 176 °F
ASTM Test
35.0 MPa

@Temperature 80.0 °C
5080 psi

@Temperature 176 °F
ISO Data
126 MPa

@Temperature -40.0 °C
18300 psi

@Temperature -40.0 °F
ASTM Test
126 MPa

@Temperature -40.0 °C
18300 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break 25 %
25 %
50mm/min, Nominal strain; ISO 527
55 %
55 %
2 in/min; ASTM Test
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
4.0 %
4.0 %
2 in/min; ASTM Test
36 %

@Temperature 120 °C
36 %

@Temperature 248 °F
ISO Data
36 %

@Temperature 120 °C
36 %

@Temperature 248 °F
ASTM Test
42 %

@Temperature 80.0 °C
42 %

@Temperature 176 °F
ISO Data
42 %

@Temperature 80.0 °C
42 %

@Temperature 176 °F
ASTM Test
Tensile Modulus 2.70 GPa
392 ksi
1mm/min; ISO 527
0.360 GPa

@Temperature 120 °C
52.2 ksi

@Temperature 248 °F
ISO Data
0.485 GPa

@Temperature 80.0 °C
70.3 ksi

@Temperature 176 °F
ISO Data
Flexural Strength 85.0 MPa
12300 psi
ISO Data
108 MPa
15700 psi
ASTM Test
17.0 MPa

@Temperature 120 °C
2470 psi

@Temperature 248 °F
ASTM Test
20.0 MPa

@Temperature 93.0 °C
2900 psi

@Temperature 199 °F
ASTM Test
30.0 MPa

@Temperature 65.0 °C
4350 psi

@Temperature 149 °F
ASTM Test
170 MPa

@Temperature -40.0 °C
24700 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 2.40 GPa
348 ksi
ISO Data
2.83 GPa
410 ksi
ASTM Test
0.305 GPa

@Temperature 120 °C
44.2 ksi

@Temperature 248 °F
ASTM Test
0.350 GPa

@Temperature 93.0 °C
50.8 ksi

@Temperature 199 °F
ASTM Test
0.500 GPa

@Temperature 65.0 °C
72.5 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 0.480 J/cm

@Temperature -40.0 °C
0.899 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.580 J/cm

@Thickness 3.17 mm
1.09 ft-lb/in

@Thickness 0.125 in
ASTM Test
Charpy Impact Unnotched NB
NB
ISO 179
5.10 J/cm²

@Temperature -30.0 °C
24.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 83.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
46.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Specific Heat Capacity 3.728 J/g-°C
0.8910 BTU/lb-°F
Melt
Thermal Conductivity 0.264 W/m-K
1.83 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75
178 °C
352 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75
65.0 °C
149 °F
ASTM Test
Flammability, UL94 V-2

@Thickness 0.700 mm
V-2

@Thickness 0.0276 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
IEC 60250
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
IEC 60250
4.1

@Frequency 1.00e+6 Hz
4.1

@Frequency 1.00e+6 Hz
ASTM Data
4.3

@Frequency 1e+9 Hz
4.3

@Frequency 1e+9 Hz
ASTM Data
Dielectric Strength 37.0 kV/mm
940 kV/in
IEC 60243-1
Dissipation Factor 0.010

@Frequency 1e+9 Hz
0.010

@Frequency 1e+9 Hz
ASTM Data
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM Data
0.010

@Frequency 100 Hz
0.010

@Frequency 100 Hz
IEC 60250
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding
Mold Temperature 80.0 °C
176 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
UL.UL-C Yes