Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 10.1 MPa | 1460 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C7000 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.1 MPa | 1460 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C70U0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.1 MPa | 1460 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 514 Perfluoroelastomer Greene Tweed’s Chemraz® 514, a perfluoroelastomer, is a white specialty compound, perfect for applications where contamination from carbon black must be prevented. Chemraz 514 offers a Shor.. |
|||
Tensile Strength at Break | 10.1 MPa | 1460 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 534 Perfluoroelastomer Chemraz®, a proprietary Greene, Tweed compound, has the broadest chemical resistance of any elastomeric material. Chemraz combines the resilience and sealing force of an elastomer with chemical r.. |
|||
Tensile Strength at Break | 10.1 MPa | 1470 psi | ASTM D412 |
Teknor Apex APEX® 2555-H Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Good FlexibilityUses-General Purpose, ProfilesAppearance-Natural Color, OpaqueForms-PelletsProcessin.. |
|||
Tensile Strength at Break | 10.1 MPa | 1470 psi | ASTM D412 |
Teknor Apex Monprene® MP-1702B Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.1 MPa | 1470 psi | ASTM D412 |
Teknor Apex Monprene® MP-1702C Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.1 - 11.7 MPa | 1470 - 1700 psi | |
Plastic Lumber from the Plastic Lumber Co. Description: Plastic Lumber is a product similar to wood that is made from recycled plastic jugs. Products will never splinter, rot, crumble or need painting. Plastic Lumber has rapidly gained accep.. |
|||
Tensile Strength at Break | 10.1 MPa | 1460 psi | |
Abatron LiquidWood® Deep Penetrating Wood Consolidant LiquidWood® is a deep penetrating wood consolidant that regenerates and waterproofs rotted, dried-out, or spongy wood. It restores structural strength and durability to wood fibers. With LiquidWood.. |
|||
Tensile Strength at Break | 10.1 MPa | 1460 psi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5730 Fluoroelastomer Composition: Ter-polymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethyleneLower fluorine version of FE 5830QProcess targets: extrusion onlyProprietary incorporated cure technologyP.. |