Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 13.8 MPa | 2000 psi | Mixed 1:2; TM R050-36 |
Resinlab® EP1215 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP1215 Clear is a two part unfilled epoxy structural adhesive designed for bonding applications requiring high strength and good impact resistance. It cures completely at room temperature.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R130AE White 41 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R999A Black Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | 510 mm/min; ASTM D412A |
PolyOne Geon™ Vinyl Flexible XV3725 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D4894 |
3M Dyneon™ CC191-HE Custom Fluoropolymer Compound
(discontinued **) This compound consists of a mixture of high elongation 23% carbon / 2% graphite blended with PTFE.Information provided by Dyneon, A 3M Company |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Manifattura Cattaneo RULON® 641 Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Tensile Strength at Break | 13.8 - 17.2 MPa | 2000 - 2500 psi | |
ITW Plexus Plexusâ„¢ MA3940 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Use with craze sensitive plastics.Information provided by Illinois Tool Works. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ISO R 527 |
Stir SpA T 2199 A (PVC) Application: Non-toxic transparent pipeInformation provided by STIR SpA |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Teknor Apex APEX® 3315-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Teknor Apex APEX® 3610-70 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: First Generation SeriesInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Teknor Apex APEX® 85-J644-H Polyvinyl Chloride, Flexible Notes: 105°C Jacket; RoHS Compliant Features: Flame Retardant; High Heat Resistance; Low gloss Uses: Communication Wire Jacketing; Patch Cord Jacketing Forms: Pellets Agency Ratings: NEC Article .. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Teknor Apex APEX® CX 2001-73 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ISO R 527 |
Stir SpA Z 70 3 AT (PVC) Application: Molding for beach footwearInformation provided by STIR SpA |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D412 |
Teknor Apex Telcar® TL-150 BLK288 Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Speci.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D412 |
Borealis FR4845 Irradiation Crosslinkable Polyethylene Compound FR4845 is an Irradiation Crosslinkable non-halogen flame retardant compound developed for the automotive wire market. Applications: FR4845 is intended for use as a 125º C rated primary insulation .. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 504E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 504 is an extrusion grade olefinic thermoplastic elastomer suitable for profile extrusion or blow molding. Characteristics of this product include excellent low temperature.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 504E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 504 is an extrusion grade olefinic thermoplastic elastomer suitable for profile extrusion or blow molding. Characteristics of this product include excellent low temperature.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DMDA-8920 NT 7 High Density Polyethylene Resin DOW DMDA-8920 NT 7 is produced using UNIPOL™ process technology. It is intended for use in a broad range of injection molding applications such as housewares, toys, food containers and pails. Info.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DNDA-7340 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-7340 NT 7 LLDPE resin is well-suited for use in blow molding applications such as small, squeezable bottles, as well as, extruded flexible hoses and tubing. DOW DMDA-7340 NT 7 resin is als.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Bayshore Vinyl Compounds BVC 6200-85 Vinyl Compound BVC 6200-85 is an economy grade flexible vinyl formulation designed for easy processing and excellent heat stability. This material will process at high rates with low temperatures and produces a s.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5520 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5520 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 13.8 - 20.7 MPa | 2000 - 3000 psi | |
Abatron AboCast 7802-1/AboCure 50-3 (80 pbw) Epoxy AboCast 7802-1 is a clear resin with low viscosity (600-800 cps.) and a weight of 9.1 lbs/gallon. AboCure 50-3 is a clear, slow converter for lower rigidity. It has an HDT of 60°C, variable ratio, .. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-40006T/4 Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-40009.5S/2 Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-40036S/2 Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-43036B Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | |
3M Controltac™ IJ380Cv3 Wrap Film with Comply™ v3 Adhesive 2-mil white, vinyl film with a luster finish; Pressure-activated adhesive for easy sliding, tacking, snap up and repositioning; Non-visible, air release channels for fast, easy, bubble-free installa.. |