Polymer Property : Creep Strength = 138 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Creep Strength	138 MPa @Temperature 816 Â°C, Time 3.60e+6 sec	20000 psi @Temperature 1500 Â°F, Time 1000 hour	0.5% Creep
Haynes 282Â® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Creep Strength	138 MPa @Temperature 593 °C, Time 3.60e+7 sec	20000 psi @Temperature 1100 °F, Time 10000 hour	1% creep
ATI Allegheny Ludlum 310 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Creep Strength	138 MPa @Temperature 593 °C, Time 3.60e+7 sec	20000 psi @Temperature 1100 °F, Time 10000 hour	1% creep
ATI Allegheny Ludlum 310H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Creep Strength	138 MPa @Temperature 593 °C, Time 3.60e+7 sec	20000 psi @Temperature 1100 °F, Time 10000 hour	1% creep
ATI Allegheny Ludlum 310S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Creep Strength	138 MPa @Temperature 593 °C, Time 3.60e+7 sec	20000 psi @Temperature 1100 °F, Time 10000 hour	1% creep
ATI Allegheny Ludlum 310Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..