ATI Allegheny Ludlum 310S Austenitic Stainless Steel

Category Metal , Ferrous Metal , Stainless Steel , T 300 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum 310S Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep deformation resistance.Applications:Heat treatment industry-conveyor belts, rollers, burner parts, refractory supports, retorts linings, oven linings, fans, tube hangers, baskets, and trays. Chemical process industry- containers for hot concentrated acids, ammonia, and sulfur dioxide. Food processing industry- used in contact with hot acetic and citric acid.Information provided by Allegheny Ludlum
Physical Properties Metric English Comments
Density 8.03 g/cc
0.290 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 624 MPa
90500 psi
ASTM E8
44.0 MPa

@Temperature 1093 °C
6380 psi

@Temperature 1999 °F
ASTM E8
81.0 MPa

@Temperature 982 °C
11700 psi

@Temperature 1800 °F
ASTM E8
155 MPa

@Temperature 871 °C
22500 psi

@Temperature 1600 °F
ASTM E8
393 MPa

@Temperature 649 °C
57000 psi

@Temperature 1200 °F
ASTM E8
484 MPa

@Temperature 538 °C
70200 psi

@Temperature 1000 °F
ASTM E8
508 MPa

@Temperature 427 °C
73700 psi

@Temperature 801 °F
ASTM E8
533 MPa

@Temperature 204 °C
77300 psi

@Temperature 399 °F
ASTM E8
Tensile Strength, Yield 27.0 MPa

@Temperature 1093 °C
3920 psi

@Temperature 1999 °F
ASTM E8
56.0 MPa

@Temperature 982 °C
8120 psi

@Temperature 1800 °F
ASTM E8
111 MPa

@Temperature 871 °C
16100 psi

@Temperature 1600 °F
ASTM E8
178 MPa

@Temperature 649 °C
25800 psi

@Temperature 1200 °F
ASTM E8
203 MPa

@Temperature 538 °C
29400 psi

@Temperature 1000 °F
ASTM E8
209 MPa

@Temperature 427 °C
30300 psi

@Temperature 801 °F
ASTM E8
254 MPa

@Temperature 204 °C
36800 psi

@Temperature 399 °F
ASTM E8
314 MPa

@Strain 0.200 %
45500 psi

@Strain 0.200 %
ASTM E8
Elongation at Break 42.6 %
42.6 %
ASTM E8
32 %

@Temperature 649 °C
32 %

@Temperature 1200 °F
ASTM E8
33.5 %

@Temperature 427 °C
33.5 %

@Temperature 801 °F
ASTM E8
35.8 %

@Temperature 204 °C
35.8 %

@Temperature 399 °F
ASTM E8
37 %

@Temperature 538 °C
37 %

@Temperature 1000 °F
ASTM E8
56.5 %

@Temperature 871 °C
56.5 %

@Temperature 1600 °F
ASTM E8
93.3 %

@Temperature 982 °C
93.3 %

@Temperature 1800 °F
ASTM E8
121 %

@Temperature 1093 °C
121 %

@Temperature 1999 °F
ASTM E8
Creep Strength 20.0 MPa

@Temperature 788 °C,
Time 3.60e+7 sec
2900 psi

@Temperature 1450 °F,
Time 10000 hour
1% creep
138 MPa

@Temperature 593 °C,
Time 3.60e+7 sec
20000 psi

@Temperature 1100 °F,
Time 10000 hour
1% creep
Rupture Strength 20.0 MPa

@Temperature 899 °C,
Time 3.60e+7 sec
2900 psi

@Temperature 1650 °F,
Time 10000 hour
138 MPa

@Temperature 593 °C,
Time 3.60e+7 sec
20000 psi

@Temperature 1100 °F,
Time 10000 hour
Modulus of Elasticity 200 GPa
29000 ksi
Poissons Ratio 0.30
0.30
calculated
Shear Modulus 77.0 GPa
11200 ksi
Thermal Properties Metric English Comments
CTE, linear 15.9 µm/m-°C

@Temperature 20.0 - 100 °C
8.83 µin/in-°F

@Temperature 68.0 - 212 °F
17.1 µm/m-°C

@Temperature 20.0 - 500 °C
9.50 µin/in-°F

@Temperature 68.0 - 932 °F
18.9 µm/m-°C

@Temperature 20.0 - 1000 °C
10.5 µin/in-°F

@Temperature 68.0 - 1830 °F
Specific Heat Capacity 0.502 J/g-°C

@Temperature 0.000 - 100 °C
0.120 BTU/lb-°F

@Temperature 32.0 - 212 °F
Thermal Conductivity 13.8 W/m-K

@Temperature 20.0 - 100 °C
95.8 BTU-in/hr-ft²-°F

@Temperature 68.0 - 212 °F
18.7 W/m-K

@Temperature 20.0 - 500 °C
130 BTU-in/hr-ft²-°F

@Temperature 68.0 - 932 °F
Component Elements Properties Metric English Comments
Carbon, C 0.080 %
0.080 %
Chromium, Cr 24 - 26 %
24 - 26 %
Iron, Fe 48.345 - 53.345 %
48.345 - 53.345 %
As Remainder
Manganese, Mn 2.0 %
2.0 %
Nickel, Ni 19 - 22 %
19 - 22 %
Phosphorous, P 0.045 %
0.045 %
Silicon, Si 1.5 %
1.5 %
Sulfur, S 0.030 %
0.030 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000780 ohm-cm

@Temperature 20.0 °C
0.0000780 ohm-cm

@Temperature 68.0 °F
Magnetic Permeability 1.02
1.02
at 200H