Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 500 MPa | 72500 psi | |
Lehmann & Voss LUVOCOM® 20/XCF/30 Polyphthalamide, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita.. |
|||
Flexural Strength | 500 MPa | 72500 psi | |
Sapco 99.7% Aluminum Oxide Information provided by Sapco. |
|||
Flexural Strength | 500 MPa | 72500 psi | Bending Strength; Dual Ring Method (0.63 mm Substrate Thickness); DIN 52292 |
CeramTec Rubalit® 708S Alumina, 96% Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste.. |
|||
Flexural Strength | 500 MPa | 72500 psi | DIN EN 843-1 |
CeramTec ZN 40 Zirconia, ZrO2-MgO ZN 40 is a zirconium oxide ceramic with an excellent surface finish and a higher strength than aluminum oxide. Its good crack resistance and anti-friction properties, combined with steel-like therma.. |
|||
Flexural Strength | >= 500 MPa | >= 72500 psi | Limit of elasticity in Bending |
CLAL-MSX SICLANIC S® TH3 Quenched Copper Alloy, 1/2 Hard, precipitation treated SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver.. |
|||
Flexural Strength | >= 500 MPa | >= 72500 psi | high temp bending |
China-Yixing Longly Refractories Slab SiC SiC series products of SiC shelf boards, SiC pillars, SiC slab, SiC seggar kiln furniture, are formed using high-quality silicon carbide materials and high temperature binders by tons of high-vibrat.. |
|||
Flexural Strength | >= 500 MPa @Diameter >=100 mm |
>= 72500 psi @Diameter >=3.94 in |
Perpendicular to laminations; IEC 1212-2 4.1 |
Hippe EP GC 41 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. High mechanical strength at moderate temperatures. Good stability of electrical properties when exposed to high relative humidity.Inform.. |
|||
Flexural Strength | 500 MPa | 72500 psi | Bending Strength; dual-ring method (0.63 mm substrate thickness); DIN 52292 |
CeramTec CeramCool® Rubalit® 708 Alumina, 96% CeramCool® is a metallized ceramic heat-sink for high power applications demonstrated by high power LED-systems. CeramCool® material characteristics: electrical insulation, high volume resistivit.. |
|||
Flexural Strength | 500 MPa | 72500 psi | Bending Strength; Double-Ring (40 mm / 20 mm / 0.63 mm); DIN EN 1288 |
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance) Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn.. |