Polymer Property : Flexural Strength = 500 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	500 MPa	72500 psi
Lehmann & Voss LUVOCOMÂ® 20/XCF/30 Polyphthalamide, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita..
Flexural Strength	500 MPa	72500 psi
Sapco 99.7% Aluminum Oxide Information provided by Sapco.
Flexural Strength	500 MPa	72500 psi	Bending Strength; Dual Ring Method (0.63 mm Substrate Thickness); DIN 52292
CeramTec Rubalit® 708S Alumina, 96% Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste..
Flexural Strength	500 MPa	72500 psi	DIN EN 843-1
CeramTec ZN 40 Zirconia, ZrO2-MgO ZN 40 is a zirconium oxide ceramic with an excellent surface finish and a higher strength than aluminum oxide. Its good crack resistance and anti-friction properties, combined with steel-like therma..
Flexural Strength	>= 500 MPa	>= 72500 psi	Limit of elasticity in Bending
CLAL-MSX SICLANIC S® TH3 Quenched Copper Alloy, 1/2 Hard, precipitation treated SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver..
Flexural Strength	>= 500 MPa	>= 72500 psi	high temp bending
China-Yixing Longly Refractories Slab SiC SiC series products of SiC shelf boards, SiC pillars, SiC slab, SiC seggar kiln furniture, are formed using high-quality silicon carbide materials and high temperature binders by tons of high-vibrat..
Flexural Strength	>= 500 MPa @Diameter >=100 mm	>= 72500 psi @Diameter >=3.94 in	Perpendicular to laminations; IEC 1212-2 4.1
Hippe EP GC 41 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. High mechanical strength at moderate temperatures. Good stability of electrical properties when exposed to high relative humidity.Inform..
Flexural Strength	500 MPa	72500 psi	Bending Strength; dual-ring method (0.63 mm substrate thickness); DIN 52292
CeramTec CeramCool® Rubalit® 708 Alumina, 96% CeramCool® is a metallized ceramic heat-sink for high power applications demonstrated by high power LED-systems. CeramCool® material characteristics: electrical insulation, high volume resistivit..
Flexural Strength	500 MPa	72500 psi	Bending Strength; Double-Ring (40 mm / 20 mm / 0.63 mm); DIN EN 1288
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance) Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn..