Polymer Property : Flexural Strength = 32800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	226 MPa	32800 psi	ASTM D790
Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi..
Flexural Strength	226 MPa	32800 psi	5 mm/min; ISO 178
Gromax BFG30-EN04B2 Nylon 6 36% Glass Filled (Dry) Information provided by Gromax Enterprises Corp.
Flexural Strength	226 MPa	32800 psi	ASTM D790
Solvay Specialty Polymers AmodelÂ® AT-1116 HS Polyphthalamide (PPA), 16% Glass Fiber (Dry) AmodelÂ® AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s..
Flexural Strength	226 MPa	32800 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON JX89626 PES LNP* STAT-KON* JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive.
Flexural Strength	226 MPa	32800 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive.
Flexural Strength	226 MPa	32800 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC (Asia Pacific) LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Flexural Strength	226 MPa	32800 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI LNP* Thermocomp* EF004 is a compound based on Polyetherimide resin containing 20% Glass Fiber.
Flexural Strength	226 MPa	32800 psi	2.8 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® XP-2140 PPS Information provided by Samsung Cheil Industries.
Flexural Strength	226 MPa	32800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66 LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding.
Flexural Strength	226 MPa	32800 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DE006ER PC LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive.
Flexural Strength	226 MPa	32800 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DE006ER PC (Asia Pacific) LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Flexural Strength	226 MPa	32800 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 754 Glass Reinforced, Flow Enhanced, PPS Alloy, UL Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	226 MPa	32800 psi	2.8 mm/min; ASTM D638
Samsung Cheil Industries Infino® XP-2140 PPS Information provided by Samsung Cheil Industries.