Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 235 MPa | 34100 psi | |
Plastcom SLOVAMID 66 GF 25 FRG 5 TS PA66, 25% glass fibre, flame retardant FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fibre and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 in accordance with UL 94. Non.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Plastcom SLOVAMID 66 GF 30 FRG 5 PA66, 30% glass fibre, flame retarder FeaturesPA 66 for injection moulding, chemically reinforced with 30 % glass fibre and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 /0,8 mm/ in accordance with .. |
|||
Flexural Strength | 235 MPa | 34100 psi | STN EN ISO 178 |
Plastcom SLOVAMID 66 GF 35 FRG 5 Polyamide 66, 35% Glass Fiber, Halogen Free Flame Retardant FeaturesPA 66 for injection moulding, chemical reinforced with 35% glass fiber and non-halogen flame retardant, with heat and flammability resistance, achieves V-0 in accordance with UL 94. Non-hal.. |
|||
Flexural Strength | 235 MPa | 34100 psi | ASTM D790 |
Quantum Composites QC-8777 41% Glass Fiber Reinforced Polyester Hybrid SMC QC-8777 is a polyester hybrid engineered structural composite molding compound designed for compression molding of components requiring high structural strength, corrosion resistance and temperature.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 1105-8000 PEEK, with carbon fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 19-7748 Polyamide 46, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 19-7912 Polyamide 46, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.Gear parts f.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 6-7595 Polyamide 12, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Especially suitable at dynamic.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/HS/BK Polyamide 66, with glass fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low warpage.Improved friction and wear behaviour. Emergency running propert.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 1105-7914 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.High chemical resistance parts, hydrolysis resi.. |
|||
Flexural Strength | 235 MPa | 34100 psi | |
Lehmann & Voss LUVOCOM® 1105-7916-1 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.High chemical resistance parts, hydrolysis resi.. |
|||
Flexural Strength | 235 MPa @Strain 3.60 % |
34100 psi @Strain 3.60 % |
d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS. |
|||
Flexural Strength | 235 MPa | 34100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 235 MPa | 34100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 235 MPa | 34100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 235 MPa | 34100 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
Flexural Strength | 235 MPa | 34100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RF007ESS PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF007ESS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.This data was supplied by SABIC-IP for.. |
|||
Flexural Strength | 235 MPa | 34100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF IX02582 PA6.12 LNP* Thermotuf* IX02582 is a compound based on Nylon 6/12 resin containing Proprietary Filler(s). Added features of this material include: High Impact. |
|||
Flexural Strength | 235 MPa | 34100 psi | at rupture; ASTM D790 |
Sumitomo Bakelite North America E 264H Long Glass Fiber Reinforced Epoxy E 264H is a high strength, long fiberglass reinforced epoxy molding compound, which features improved flow in transfer molding.Information provided by Sumitomo Bak North America, Inc. |
|||
Flexural Strength | 235 MPa | 34100 psi | GB/T 9341-2008 |
Sichuan Deyang Haton® hMR60DL Polyphenylene Sulfide, Glass & Mineral Reinforced Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Flexural Strength | 235 MPa | 34100 psi | ISO 178-93 |
Wellman Wellamid® GF1662-GY1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66/6Information provided by Wellman. |
|||
Flexural Strength | 235 MPa | 34100 psi | ISO 178-93 |
Wellman Wellamid® GF33-66 XE-NBK1 33% Glass Fiber Reinforced, Engineering Grade Nylon 66 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 235 MPa | 34100 psi | dry; ISO 178 |
DSM Akulon® K224-G6-FC 99.99.99 PA6-GF30 30% Glass Reinforced, Food Contact Grade |
|||
Flexural Strength | 235 MPa | 34100 psi | dry; ISO 178 |
DSM Akulon® K224-G6-FC BK00001 PA6-GF30 30% Glass Reinforced, Food Contact Grade |
|||
Flexural Strength | 235 MPa | 34100 psi | ASTM D790, ISO 178 |
EPICHEM Epinyl PA 66 GF 30 H Polyamide 66, 30% Glass, Heat Stabilized Characteristics: 30% glass fibre filled |
|||
Flexural Strength | 235 MPa | 34100 psi | ASTM D790, ISO 178 |
EPICHEM Epinyl PA 66 GF 30 Polyamide 66, 30% Glass Characteristics: 30% glass fibre filled |
|||
Flexural Strength | 235 MPa | 34100 psi | 2 mm/min; ISO 178 |
Eurostar Staramide RF007ESS PA66/6, 35% Glass Filled, Injection Molded Staramide RF007ESS is a 35% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as RF1007EMHS)Information provided by Eurostar. |
|||
Flexural Strength | 235 MPa | 34100 psi | Wet; ASTM D790 |
Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66 43% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Mechanical and electrical parts such as micromotors, automotive parts such as radiator tanks and shift leversInformation provi.. |
|||
Flexural Strength | 235 MPa | 34100 psi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Dry, 20% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Flexural Strength | 235 MPa | 34100 psi | ASTM D790 |
Ashley Polymers Ashlene® 830L-33G Nylon 6, 33% Glass Reinforced A 33% glass fiber reinforced Nylon 6 designed to provide a high flexural modulus and good dimensional stability while maintaining the ease of processing associated with Nylon 6 type materials.Data p.. |