Polymer Property : Flexural Strength = 16.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	16.0 MPa	2320 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Nima™ HL 18400 HDPE High Density Polyethylene - Halogenated FR compound with good impact resistance. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepa..
Flexural Strength	16.0 MPa	2320 psi
Quadrant EPP TIVAR® Dryslide PE-UHMW + internal lubricant + other additives (ISO Data) Thanks to the lubricant built into a PE-UHMW matrix with higher molecular weight, TIVAR DrySlide offers a lower coefficient of friction and enhanced wear and abrasion resistance than TIVAR 1000. The..
Flexural Strength	16.0 MPa	2320 psi
Quadrant EPP TIVAR® DS PE-UHMW + additives (ISO Data) TIVAR DS is a modified PE-UHMW with extremely high molecular weight. The latter in combination with a particular manufacturing process result in a PE-UHMW grade with superior wear and abrasion resis..
Flexural Strength	16.0 MPa	2320 psi
Quadrant EPP TIVAR® H.O.T. PE-UHMW + specific additives (ISO Data) TIVAR H.O.T. [Higher Operating Temperature] is formulated to maintain inherent PE-UHMW key properties over an extended service temperature range, in this way considerably increasing part life in low..
Flexural Strength	16.0 MPa	2320 psi	ASTM D790
LG Chemical LUPOL TE-5005H Thermoplastic Elastomer Alloy, Dimensional Stability LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive exterior parts.Information Provided by LG Chem
Flexural Strength	16.0 MPa	2320 psi	ISO 178
SABIC Innovative Plastics LNP Stat-kon TD000 LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	16.0 MPa	2320 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON TD000 PU LNP* STAT-KON* TD000 is an unfilled compound based on Polyurethane resin. Added feature of this material is: Electrically Conductive.
Flexural Strength	16.0 MPa	2320 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Flexural Strength	16.0 MPa	2320 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific) LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Flexural Strength	16.0 MPa	2320 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP) LNP* THERMOCOMP* 2X03624H is a compound based on FEP resin containing Proprietary Filler(s).
Flexural Strength	16.0 MPa	2320 psi	Olsen; ASTM D747
UBE F022 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	16.0 MPa	2320 psi	Olsen; ASTM D747
UBE F022NH Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	16.0 MPa	2320 psi	Olsen; ASTM D747
UBE F120N Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	16.0 MPa	2320 psi	ASTM D790
UBE UBESTA® 3030JI7 Plasticized Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: low migrationInformation provided by UBE.
Flexural Strength	16.0 MPa	2320 psi	ASTM D790
UBE PAE1201U Nylon Elastomer Description: UBESTA Nylon 12 ElastomerInformation provided by UBE.
Flexural Strength	16.0 MPa	2320 psi	ASTM D790
UBE UBESTA® 3030JNU Short Cycle Time Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System..
Flexural Strength	16.0 MPa	2320 psi	cond; ISO 178
DSM Novamid® ST145 NAT PA6-I Impact Modified, Injection Molding
Flexural Strength	16.0 MPa	2320 psi	2 mm/min; ISO 178
Eurostar Staramide AG3X3 PA66, Glass Fiber Reinforced, Impact Modified, Injection Molding Staramide AG3X3 is an Impact Modified, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	16.0 MPa	2320 psi	ASTM D790
Aclo Accutech Polypropylene Copolymer CP0437C10L Calcium Reinforced
Flexural Strength	16.0 MPa	2320 psi	ASTM D790
Aclo Accutech Polypropylene Copolymer CP0437C20L Calcium Reinforced
Flexural Strength	16.0 MPa	2320 psi	SAE J949
Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Flexural Strength	16.0 MPa	2320 psi	cond.; ISO 178
Azoty Tarnow™ Tarnamid® T-27 MCS HI Polyamide 6 - Impact Modified Very high impact resistance, cold impact grade (to -40°C). Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has t..