Material Notes:
Description: UBESTA Nylon 12 ElastomerInformation provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Melt Flow | 8.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
8.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
| Flexural Modulus | 0.360 GPa | 52.2 ksi | ASTM D790 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Injection Molding |
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
| Compression Ratio | 2.5-3.5:1 | Injection Molding |
| min 3:1 | For 8x1 mm Tube Extrusion | |
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
| Die Width | 300 mm | For T-Die Cast Film Extrusion |
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
| Flight Depth in the Feeding Zone | 10-15% of Screw Diameter | Injection Molding |
| Flight Depth in the Metering Zone | 5-7% of Screw Diameter | Injection Molding |
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
| min 20:1 | Injection Molding | |
| Length of Compression Zone | 25-45% of total screw length | Injection Molding |
| 30% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Feeding Zone | 20-40% of total screw length | Injection Molding |
| 30-40% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
| 35-45% of total screw length | Injection Molding | |
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
| Peripheral screw speed | 10 m/min | Injection Molding |
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PP CONC 36 NAT S Polypropylene, Unspecified (PP, Unspecified)
- ExxonMobil LL 6235.19 Injection Molding Resin (discontinued **)
- PolyOne Edgetek® AT-30GF/000 FDA Acetal-Copolymer, Glass Filled (discontinued **)
- Latrobe Lescalloy® 6305 VAC-ARC ; High Strength Alloy Steel
- Abatron AboWeld 55-22/AboCure 55-22 Epoxy
- 3M Scotchcal™ 1000-46 Graphic Film
- API Megol AM T A SEBS Adhesion Modified Overmolding for Polar Polymers
- Teknor Apex Monprene® MP-2691A Thermoplastic Elastomer
- A. Schulman POLYBLAK™ 4479-01 Black Color Concentrate, 50% Carbon Black Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved