- Polymer Property : Modulus of Elasticity = 28000 ksi
Polymer Property : Modulus of Elasticity = 28000 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 500 °C |
28000 ksi @Temperature 932 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 600 °C |
28000 ksi @Temperature 1110 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 600 °C |
28000 ksi @Temperature 1110 °F |
|
| Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 600 °C |
28000 ksi @Temperature 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 600 °C |
28000 ksi @Temperature 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | In Tension |
| HP Alloys Nitronic® 50 Austenitic Stainless, Annealed Annealed applies to tensile, impact, and hardness values and are for 3/4 in. diameter samples; other properties are typical of this alloy.Nitronic® 50 Stainless Steel provides a combination of co.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | In Tension |
| HP Alloys Nitronic® 50 Austenitic Stainless, Level 2 Cold Worked Cold Worked applies to tensile values and are for 0.25 to 4 in. diameter samples; other properties are typical of this alloy.Nitronic® 50 Stainless Steel provides a combination of corrosion resis.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | In Tension |
| HP Alloys Nitronic® 50 Austenitic Stainless, Level 3 Cold Worked Cold Worked applies to tensile values and are for 0.25 to 2.4 in. diameter samples; other properties are typical of this alloy.Nitronic® 50 Stainless Steel provides a combination of corrosion res.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | In Tension |
| HP Alloys Nitronic® 50 Austenitic Stainless, Level 4 Cold Worked Cold Worked applies to tensile values and are for 1/4 to 2 in. diameter samples; other properties are typical of this alloy.Nitronic® 50 Stainless Steel provides a combination of corrosion resist.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | Tension |
| Crucible Steel 20 Cb Plus Stainless Steel Crucible 20 Cb Plus is a non-hardenable stabilized stainless steel with exceptional resistance to sulfuric, phosphoric, and nitric acid. This grade also has good resistance to stress corrosion crack.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | Tension |
| Crucible Steel 303 Plus Chromium-Nickel Steel Crucible 303 Plus is a non-hardenable austenitic chromium-nickel steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | Tension |
| Crucible Steel 303 SE Chromium-Nickel Steel Crucible 303 SE is a non-hardenable austenitic chromium-nickel steel to which selenium has been added to improve machinability and non-galling characteristics. This grade is non-magnetic in the anne.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | Tension |
| Crucible Steel 348 Chromium-Nickel Steel Crucible 348 is a non-hardenable austenitic chromium-nickel steel which are particularly adaptable for use at temperatures between 800 and 1650°F. This grade is non-magnetic in the annealed conditi.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | tension |
| AK Steel 301 Austenitic Stainless steel AK Steel 301 provides high strength and good ductility when cold worked. It is a modification of AK Steel 302 to increase the cold work-hardening range, to permit higher tensile strengths to be ach.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | tension |
| AK Steel 304L Austenitic Stainless steel AK Steel 304L is an extra low-carbon variation of Type 304, that eliminates carbide precipitation due to welding. AK Steel 304L can be used in the "as-welded" condition, even in severe corrosive co.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | In Tension |
| Carpenter 20Cb-3® Stainless Steel, Strip, Annealed at 1750°F (955°C) then Water Quenched Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | |
| Assab Steels ASSAB XW-42 Cold Work Steel XW-42 is a high-carbon, high chromium tool steel alloyed with molybdenum and vanadium characterized by:High wear resistanceHigh compressive strength High hardness after hardeningGood through-hardeni.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | |
| Carlson Nitronic® 30® Austenitic Stainless Steel General DescriptionNitronic 30 is a nitrogen-strengthened austenitic stainless steel developed for applications requiring good aqueous corrosion resistance combined with good resistance to abrasive .. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | as rolled longitudinal |
| ATI Allegheny Ludlum Stainless Steel Type 301, 1/4 Hard (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | |
| ATI Allegheny Ludlum AL 20™ Sheet and Strip Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im.. |
|||
| Modulus of Elasticity | 193 GPa @Temperature 600 °C |
28000 ksi @Temperature 1110 °F |
|
| Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | in tension |
| ATI Allegheny Ludlum Stainless Steel Type 347 (UNS S34700) AL 347 is a stabilized stainless steel which offers excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800° to 1500°.. |
|||
| Modulus of Elasticity | 193 GPa | 28000 ksi | |
| Materion AlBeMet® AM 162 Extruded Bar, Annealed Mechanical property values below are in the longitudinal direction; transverse values generally lower. This is a powder metallurgical product produced by gas atomization available as rod, bar, tube.. |
|||