Polymer Property : Modulus of Elasticity = 18600 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	128 GPa @Temperature 1000 Â°C	18600 ksi @Temperature 1830 Â°F
Haynes HR-120Â® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Modulus of Elasticity	128 GPa @Temperature 1000 Â°C	18600 ksi @Temperature 1830 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1200Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Modulus of Elasticity	128 GPa @Temperature 1000 Â°C	18600 ksi @Temperature 1830 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1400Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Modulus of Elasticity	128 GPa @Temperature 1000 Â°C	18600 ksi @Temperature 1830 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1600Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Modulus of Elasticity	128 GPa @Temperature 1000 Â°C	18600 ksi @Temperature 1830 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1800Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Modulus of Elasticity	128 GPa @Temperature 1000 Â°C	18600 ksi @Temperature 1830 Â°F
Haynes HR-120Â® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Modulus of Elasticity	128 GPa	18600 ksi	Typical
TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Annealed Sheet/Plate & Billet/Bar Low Cost, Multipurpose Alloy. Tensile property data below for Annealed Sheet/Plate & Billet/Bar.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, but wit..
Modulus of Elasticity	128 GPa	18600 ksi	Typical
TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Beta Forged Low Cost, Multipurpose Alloy. Tensile/toughness property data below for Beta Forged, RA material.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, but wi..
Modulus of Elasticity	128 GPa	18600 ksi
CMW® 73 Copper Alloy CMW® 73 material is a heat treatable copper base alloy having extremely high hardness and strength coupled with fair electrical and thermal conductivity. The extremely high hardness, strength and w..
Modulus of Elasticity	128 GPa	18600 ksi	Ultrasonic
CeramTec 547 Cordierite (2MgO-2Al2O3-5SiO2) Te value is 670°C. Hasselman Thermal Shock value is 800 K.Data provided by CeramTec North America.
Modulus of Elasticity	128 GPa	18600 ksi	Typical
TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Alpha-Beta Forged, RA Low Cost, Multipurpose Alloy. Tensile/toughness property data below for Alpha-Beta Forged, RA material.Features: Properties and processing characteristics equivalent to or better than TIMETAL 6-4, ..